Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 20.0 - 55.0 MPa @Temperature 60.0 - 120 °C |
2900 - 7980 psi @Temperature 140 - 248 °F |
Average value: 38.3 MPa Grade Count:1 |
Overview of materials for Polyphenylene Ether, Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, Mineral Filled". Each property range of values reported is minimum and maximum valu.. |
|||
Tensile Strength, Ultimate | 20.0 - 55.0 MPa @Temperature 160 - 160 °C |
2900 - 7980 psi @Temperature 320 - 320 °F |
Average value: 67.6 MPa Grade Count:2 |
Overview of materials for Polysulfone (PSU) This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone". Each property range of values reported is minimum and maximum values of appropriate MatWeb.. |
|||
Tensile Strength, Ultimate | 20.0 - 55.0 MPa @Strain 1.00 - 2.00 % |
2900 - 7980 psi @Strain 1.00 - 2.00 % |
Average value: 67.6 MPa Grade Count:2 |
Overview of materials for Polysulfone (PSU) This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone". Each property range of values reported is minimum and maximum values of appropriate MatWeb.. |
|||
Tensile Strength, Ultimate | 19.0 - 55.0 MPa | 2760 - 7980 psi | Average value: 47.8 MPa Grade Count:18 |
Overview of materials for ECTFE Fluoropolymer This property data is a summary of similar materials in the MatWeb database for the category "ECTFE Fluoropolymer". Each property range of values reported is minimum and maximum values of appropriat.. |
|||
Tensile Strength, Ultimate | 25.0 - 55.0 MPa @Temperature 60.0 - 150 °C |
3630 - 7980 psi @Temperature 140 - 302 °F |
Average value: 38.4 MPa Grade Count:2 |
Overview of materials for Nylon 66, Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Bead Filled". Each property range of values reported is minimum and maximum values of ap.. |
|||
Tensile Strength, Ultimate | 41.0 - 55.0 MPa | 5950 - 7980 psi | |
Cosmic Plastics 6130F Long Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 41.0 - 55.0 MPa | 5950 - 7980 psi | |
Cosmic Plastics 6230 Long Glass Fiber Filled Iso Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 35.0 - 55.0 MPa @Temperature 60.0 - 120 °C |
5080 - 7980 psi @Temperature 140 - 248 °F |
Average value: 43.3 MPa Grade Count:1 |
Overview of materials for Polybutylene Terephthalate (PBT), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Mineral Filled". Each property range of values reported is minimum and.. |
|||
Tensile Strength, Ultimate | 50.0 - 55.0 MPa @Temperature 160 - 160 °C |
7250 - 7980 psi @Temperature 320 - 320 °F |
Average value: 78.5 MPa Grade Count:1 |
Overview of materials for Polysulfone, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are inc.. |
|||
Tensile Strength, Ultimate | 50.0 - 55.0 MPa @Strain 1.00 - 1.70 % |
7250 - 7980 psi @Strain 1.00 - 1.70 % |
Average value: 78.5 MPa Grade Count:1 |
Overview of materials for Polysulfone, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are inc.. |
|||
Tensile Strength, Ultimate | 41.0 - 55.0 MPa | 5950 - 7980 psi | |
Cosmic Plastics 6130 Long Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 41.0 - 55.0 MPa | 5950 - 7980 psi | |
Cosmic Plastics 6230F Long Glass Fiber Filled Iso Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 44.0 - 55.0 MPa | 6380 - 7980 psi | Average value: 50.6 MPa Grade Count:5 |
Overview of materials for Phenolic, Novolac, Mineral/Cellulose Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral/Cellulose Filled". Each property range of values reported is minimum and maxi.. |