Overview of materials for PVC, Sheet Grade
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Sheet Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Overview of materials for PVC, Sheet Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "PVC, Sheet Grade". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 - 1.65 g/cc | 0.0415 - 0.0596 lb/in³ | Average value: 1.33 g/cc Grade Count:36 |
| ASTM Color | -15.8 - 96.7 | -15.8 - 96.7 | Average value: 25.5 Grade Count:8 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 76.0 - 112 | 76.0 - 112 | Average value: 98.3 Grade Count:6 |
| Hardness, Shore A | 53.0 - 89.0 | 53.0 - 89.0 | Average value: 75.4 Grade Count:15 |
| Hardness, Shore D | 68.0 - 83.0 | 68.0 - 83.0 | Average value: 79.0 Grade Count:17 |
| Tensile Strength, Ultimate | 9.81 - 52.0 MPa | 1420 - 7540 psi | Average value: 24.6 MPa Grade Count:28 |
| Tensile Strength, Yield | 37.9 - 50.4 MPa | 5500 - 7310 psi | Average value: 42.9 MPa Grade Count:8 |
| Elongation at Break | 15.0 - 350 % | 15.0 - 350 % | Average value: 202 % Grade Count:19 |
| Modulus of Elasticity | 2.55 - 2.82 GPa | 370 - 409 ksi | Average value: 2.70 GPa Grade Count:8 |
| Flexural Yield Strength | 62.1 - 86.0 MPa | 9000 - 12500 psi | Average value: 74.3 MPa Grade Count:10 |
| Flexural Modulus | 2.23 - 3.31 GPa | 323 - 480 ksi | Average value: 2.68 GPa Grade Count:11 |
| Izod Impact, Notched | 0.907 - 8.01 J/cm | 1.70 - 15.0 ft-lb/in | Average value: 2.90 J/cm Grade Count:10 |
| Izod Impact, Unnotched | 0.26695 - 0.26695 J/cm @Temperature -40.0 - -40.0 °C |
0.50011 - 0.50011 ft-lb/in @Temperature -40.0 - -40.0 °F |
Average value: 0.267 J/cm Grade Count:1 |
| Falling Dart Impact | 10.8466 - 10.8466 J @Temperature -40.0 - -40.0 °C |
8.00001 - 8.00001 ft-lb @Temperature -40.0 - -40.0 °F |
Average value: 10.8 J Grade Count:1 |
| Dart Drop Total Energy | 46.7 - 161 J/cm | 0.0875 - 0.302 ft-lb/mil | Average value: 85.5 J/cm Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 63.1 - 99.0 µm/m-°C | 35.1 - 55.0 µin/in-°F | Average value: 74.4 µm/m-°C Grade Count:9 |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 - 75.6 °C | 129 - 168 °F | Average value: 67.1 °C Grade Count:12 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:7 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.50 - 15.0 % | 2.50 - 15.0 % | Average value: 7.83 % Grade Count:3 |
| Transmission, Visible | 78.0 - 90.0 % | 78.0 - 90.0 % | Average value: 84.3 % Grade Count:3 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 210 °C | 360 - 410 °F | Average value: 196 °C Grade Count:6 |