NOVA Chemicals Sclair® 10B Octene VLDPE Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Very Low Density Polyethylene (VLDPE) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 10B Octene VLDPE Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: Low gel, excellent sealability, excellent dart impact, excellent clarity.Applications: Co-extrusion.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.911 g/cc | 0.0329 lb/in³ | ASTM D792 |
| Melt Flow | 0.77 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.77 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 7.00 MPa | 1020 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 7.00 MPa | 1020 psi | ASTM D882 |
| Film Elongation at Break, MD | 500 % | 500 % | ASTM D882 |
| Film Elongation at Break, TD | 1000 % | 1000 % | ASTM D882 |
| Secant Modulus, MD | 0.145 GPa | 21.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.135 GPa | 19.6 ksi | ASTM D882 |
| Coefficient of Friction | >= 1.0 | >= 1.0 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 16.0 g/micron | 406 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 21.0 g/micron | 533 g/mil | ASTM D1922 |
| Dart Drop | 28.0 g/micron | 711 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 46.0 MPa | 6670 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 7.0 % @Thickness 0.0250 mm |
7.0 % @Thickness 0.000984 in |
ASTM D1003 |
| Gloss | 60 % | 60 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 215 - 225 °C | 419 - 437 °F |
Users viewing this material also viewed the following:
- LG Chemical SEETEC H1500 Polypropylene Homopolymer
- Techmer ES HiFill FR® PET GF15 IM FR X 15% Glass Filled
- Saint-Gobain Chemfab® TCKGN Heavyweight Rough Surface Belting
- Polyram Bondyram® 1101 Maleic Anhydride Modified Homo Propylene
- A. Schulman ComAlloy® E-13370 Lubricated Reinforced Polyester Alloy
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 5 PHR Di-Cup 40C
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 30 PHR Fumed Silica - Wacker HK N20
- Fainplast Compounds PG 60 Flexible PVC, Extrusion Modified with Rubber
- SABIC Innovative Plastics PPO 630 PPO
- Mid-Mountain Materials THERMOSEAL® FIBERPAK® M77HS Moldable
Copyright © lookpolymers.com All Rights Reserved