NOVA Chemicals Novapol® TD-9022-D Super Hexene Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE)
Manufacturer NOVA Chemicals
Trade Name Novapol®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Novapol® TD-9022-D Super Hexene Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Excellent dart impact, High strength, High toughnessApplications: Retail trash bagsAdditives: Process stabilizer, Slip/antiblockFilm properties are typical of blown film extruded at a blowup ratio of 2.5:1, but are dependent upon operating conditions.Information provided by NOVA Chemicals.
Physical Properties Metric English Comments
Density 0.917 g/cc
0.0331 lb/in³
ASTM D792
Melt Flow 0.90 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.90 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.0 MPa
1450 psi
ASTM D882
Film Tensile Strength at Yield, TD 11.0 MPa
1600 psi
ASTM D882
Film Elongation at Break, MD 550 %
550 %
ASTM D882
Film Elongation at Break, TD 700 %
700 %
ASTM D882
Secant Modulus, MD 0.160 GPa
23.2 ksi
at 1%; ASTM D882
Secant Modulus, TD 0.190 GPa
27.6 ksi
at 1%; ASTM D882
Impact 60
60
J/mm; NOVA Chemicals Puncture test
Coefficient of Friction <= 0.20
<= 0.20
ASTM D1894
Elmendorf Tear Strength, MD 18.0 g/micron
457 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 24.0 g/micron
610 g/mil
ASTM D1922
Dart Drop 22.0 g/micron
559 g/mil
F<sub>50</sub>, ASTM D1709/A
Film Tensile Strength at Break, MD 42.0 MPa
6090 psi
ASTM D882
Film Tensile Strength at Break, TD 35.0 MPa
5080 psi
ASTM D882