Polymer Property : Film Tensile Strength at Break, MD = 6090 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
SABIC 726 Series Linear Low Density Polyethylene for Blown Film Product Description: 726 series resins are fractional index Linear Low Density Polyethylene grades suitable for blown film applications. Films produced using these resins give a relatively higher ..
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ISO 527-3
Polimeri Europa Flexirene® FG 20 U Butene Copolymer Linear Low Density Polyethylene Flexirene FG 20 U is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for blown film extrusion.Main Applications: Flexirene FG 20 U is recommended for the ..
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ISO 527-3
Polimeri Europa Flexirene® FG 23 U Butene Copolymer Linear Low Density Polyethylene Flexirene FG 23 U is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for blown film extrusion.Flexirene FG 23 U represents the version of Flexirene FG 20 U..
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
NOVA Chemicals Novapol® TD-9022-C Superhexene LLDPE Puncture value is 60 J/mm. Additive Package: Antiblock.Applications: industrial liners, heavy duty packaging.Film properties are typical of 25 µm blown film extruded at a blow-up ratio of 2.5:1, b..
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
NOVA Chemicals Novapol® TD-9022-D Super Hexene Film Resin Excellent dart impact, High strength, High toughnessApplications: Retail trash bagsAdditives: Process stabilizer, Slip/antiblockFilm properties are typical of blown film extruded at a blowup ratio o..
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
NOVA Chemicals Sclair® 19C Homopolymer HDPE Film Resin Film Properties. Features: Good stiffness, good barrier, high clarity, narrow MWD.Applications: Lamination, co-extrusion.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ISO 527-3
Polimeri Europa Clearflex® H&T CMH 108 Octene Copolymer Linear Low Density Polyethylene Clearflex H&T CMH 108 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants, suitable for cast film extrusion. Stretch films obtained from Clearflex H&T CMH 108 show e..
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
NOVA Chemicals Sclair® 11F2 Butene LLDPE Film Resin (discontinued **) Film Properties. Features: Low gel, high clarity, good seal characteristics.Applications: Liquid packaging, specialty blending, general purpose sealant.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
NOVA Chemicals Sclair® 11P2 Butene LLDPE Film Resin (discontinued **) Film Properties. Features: Low gel, excellent seal characteristics, easy processability.Applications: Specialty lamination, co-extrusion.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
NOVA Chemicals Sclair® 11P3 Butene LLDPE Film Resin (discontinued **) Film Properties. Features: Low gel, excellent seal characteristics, easy processability.Applications: Specialty lamination, co-extrusion.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
NOVA Chemicals Sclair® 11P4 Butene LLDPE Film Resin (discontinued **) Film Properties. Features: Low gel, excellent sealing characteristics, easy processability.Applications: Specialty lamination, co-extrusion.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
NOVA Chemicals Sclair® 11U4 Butene LLDPE Film Resin (discontinued **) Film Properties. Features: Low gel, good clarity, easy processability.Applications: Bread bags, HDPE bottle sleeves, specialty blending.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
Iran Petrochemical (PCC) Arak 0410AA LLDPE (discontinued **) Information provided by Iran Petrochemical Commercial Co.
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
Chevron Phillips HiD® 9662 HDPE Blown Film Resin (discontinued **) Resin Type: Linear Polyethylene HomopolymerCharacteristics: Unique Molecular Architecture Gives Outstanding Moisture Barrier Properties, Excellent Film Strength and Toughness for a Homopolymer, Give..
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
NOVA Chemicals Sclair® 14B3 Butene LMDPE Film Resin (discontinued **) Film Properties. Features: Low gel, good clarity, heat resistance and barrier properties.Applications: Lamination, co-extrusion.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
NOVA Chemicals Sclair® 14K1 Octene LMDPE Film Resin (discontinued **) Film Properties. Features: Low gel, excellent optics, good moisture barrier.Applications: Cast overwrap film.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
NOVA Chemicals Sclair® 14K3 Octene LMDPE Film Resin (discontinued **) Film Properties. Features: Low gel, excellent optics, good moisture barrier.Applications: Cast overwrap film.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882-02
Ipiranga Petrochem LB 0117 LLDP IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and ba..
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ISO 1184
SIDPEC EGYPTENEÂ® LL 0205 AF LLDPE Film Applications:Heavy duty sacks, mulch filmsStretch film, liners, geomembraneFilm properties were measured on 38 micron film extruded at a blow up ratio of 2:1.Information provided by Interchim s.r.l...
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi
UBE 5033B Air Blown Nylon 6/66 Film Specialties: Standard nylon 6/66Medium shrink, Low slipApplications: Best for Middle layer usageProcessing: Top web (Air blown)Thermoforming (T-die)Information provided by UBE.
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi
UBE 5034FDX33 Air Blown Nylon 6/66 Film Specialties: High transparencyLow neck-inNucleated typeApplications: Suitable for T-die,Water and Air blown process Processing: Shrink bags (Water) Pouch ( Air blown) Information provided by UBE.
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
Eastman Eastman Embrace Copolyester for Shrink Film Applications:Flexible packagingIV containersLabels to fit high contour containersShrink packagingWrap around designKey Attributes:Excellent clarityExcellent printabilityGood chemical resistanceGood ..
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
Chevron Phillips MarFlex® 9659 HDPE Blown Film Resin Resin Type: Linear Polyethylene HomopolymerCharacteristics: Unique Molecular Architecture Gives Outstanding Moisture Barrier Properties, Excellent Film Strength and Toughness for a Homopolymer, Give..
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
Huntsman Rexell® H3108 Cast Film Extrusion LLDPE (discontinued **) Linear low density octene copolymerApplications: Cast film extrusionFilm properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
Huntsman Rexell® L3102 Blown Film Extrusion LLDPE (discontinued **) Linear-low density copolymer, cast film extrusion, FDA compliant.Features: Good impact and puncture resistance with excellent optics and sealability.Applications: Laminated and coextruded films for ..
Film Tensile Strength at Break, MD	>= 42.0 MPa	>= 6090 psi
Iran Petrochemical (PCC) Tabriz 0410AA LLDPE (discontinued **) Information provided by Iran Petrochemical Commercial Co.
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
NOVA Chemicals Sclair® 14B1 Butene LMDPE Film Resin (discontinued **) Film Properties. Features: Low gel, good clarity, heat resistance and barrier properties.Applications: Lamination, co-extrusion.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	blown films; ISO 527-3
Borealis Bormod™ HC904CF Polypropylene Bormod™ BJ368MO is a polypropylene copolymer characterized by good flow, and optimum combination of high stiffness and high impact strength. The material is nucleated with Borstar® Nucleation Tech..