Lotte Chemical Titan TITANCEED® mL1064 Linear low density polyethylene resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lotte Chemical Titan TITANCEED® mL1064 Linear low density polyethylene resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Titanceed® mL1064 is a pelleted metallocene linear low density polyethylene resin formulated with antioxidant. Films made from Titanceed® mL1064 have outstanding tensile, impact and puncture strength. The superior strength properties along with excellent draw ability makes this a very versatile packaging film resin.Applications: Blown stretch, shipping sacks, heavy duty bags, food packaging, laminations and multilayer packaging film.Advantages: Superior strength and excellent draw ability.Information provided by Titan Chemicals
Physical Properties Metric English Comments
Base Resin Density 0.918 g/cc
0.0332 lb/in³
ASTM D1505
Thickness 25.0 microns
0.984 mil
extruded at 2.5:1 BUR
Base Resin Melt Index 1.0 g/10 min
1.0 g/10 min
I<sub>2</sub>; ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 450 %
450 %
ASTM D882
Film Elongation at Break, TD 500 %
500 %
ASTM D882
Elmendorf Tear Strength, MD 13.0 g/micron
330 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 15.0 g/micron
381 g/mil
ASTM D1922
Dart Drop 23.0 g/micron
584 g/mil
ASTM D1709A
Film Tensile Strength at Break, MD 53.9 MPa
7820 psi
ASTM D882
Film Tensile Strength at Break, TD 34.3 MPa
4970 psi
ASTM D882
1% Secant Modulus, MD 147.10 MPa
21335 psi
ASTM D882
1% Secant Modulus, TD 156.90 MPa
22757 psi
ASTM D882
Optical Properties Metric English Comments
Haze 15 %
15 %
ASTM D1003
Gloss 40 %
40 %
45°; ASTM D2457
Processing Properties Metric English Comments
Melt Temperature 180 - 200 °C
356 - 392 °F
Blow-up Ratio (BUR) 2.0 - 3.0
2.0 - 3.0