Lanxess Pocan® T 7141 000000 PET + PBT, 40% Glass Fiber/Mineral

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET)
Manufacturer Lanxess
Trade Name Pocan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Pocan® T 7141 000000 PET + PBT, 40% Glass Fiber/Mineral.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PET + PBT, 40% glass fibers/mineral, injection molding, improved flowability, high thermal dimensional stabilityInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.70 g/cc
1.70 g/cc
ISO 1183
Bulk Density 0.900 g/cc
0.0325 lb/in³
ISO 60
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0020 cm/cm
0.0020 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0010 cm/cm
0.0010 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0070 cm/cm
0.0070 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Melt Flow 25 g/10 min

@Load 2.16 kg,
Temperature 280 °C
 25 g/10 min

@Load 4.76 lb,
Temperature 536 °F
 ISO 1133-1
Mechanical Properties Metric English Comments
Tensile Strength at Break 125 MPa
18100 psi
ISO 527-1, -2; 5 mm/min
Elongation at Break 1.6 %
1.6 %
ISO 527-1, -2; 5 mm/min
Tensile Modulus 12.0 GPa
1740 ksi
ISO 527-1, -2; 1 mm/min
Flexural Strength 175 MPa

@Strain 2.00 %
 25400 psi

@Strain 2.00 %
 2 mm/min; ISO 178-A
Flexural Modulus 11.0 GPa
1600 ksi
2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
<= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1A
Izod Impact, Unnotched (ISO) 35.0 kJ/m²

@Temperature 23.0 °C
 16.7 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1U
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 11.1 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
CTE, linear, Transverse to Flow 50.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 27.8 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
Melting Point 260 °C
500 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75-1, -2
Vicat Softening Point 220 °C

@Load 5.10 kg
 428 °F

@Load 11.2 lb
 120°C/hour; ISO 306
Glow Wire Test 750 °C

@Diameter 0.800 mm
 1380 °F

@Diameter 0.0315 in
 GWFI; IEC 60695-2-12
750 °C

@Diameter 1.50 mm
 1380 °F

@Diameter 0.0591 in
 GWFI; IEC 60695-2-12
750 °C

@Diameter 3.00 mm
 1380 °F

@Diameter 0.118 in
 GWFI; IEC 60695-2-12
775 °C

@Diameter 0.800 mm
 1430 °F

@Diameter 0.0315 in
 GWIT; IEC 60695-2-13
775 °C

@Diameter 1.50 mm
 1430 °F

@Diameter 0.0591 in
 GWIT; IEC 60695-2-13
775 °C

@Diameter 3.00 mm
 1430 °F

@Diameter 0.118 in
 GWIT; IEC 60695-2-13
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
280 °C
536 °F
for test specimens; ISO 294
Mold Temperature 110 °C
230 °F
for test specimens; ISO 294
100 - 130 °C
212 - 266 °F
Drying Temperature 120 °C
248 °F
Dry Time 4 - 8 hour
4 - 8 hour
Moisture Content 0.00 - 0.020 %
0.00 - 0.020 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 7792-1-PET+PBT, GHMR, 07-120, (GF+MD)40