LNP ULTEM® SMU5831 Polyetherimide, 30% CarbonGlassMineral Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), Glass + Carbon Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LNP ULTEM® SMU5831 Polyetherimide, 30% CarbonGlassMineral Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ESD characteristics for ultra high-heat applications. Will be UC3010H.Features: High Heat ResistanceForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 131 MPa | 19000 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 3.9 % | 3.9 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 157 MPa | 22800 psi | (102 mm Span) 3mm/min; ASTM D790 |
| Flexural Modulus | 10.3 GPa | 1490 ksi | (102 mm Span) 3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm | 0.701 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 223 °C @Thickness 6.35 mm |
433 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1e+05 | 1e+05 | ASTM D257 |
| Static Decay | <= 0.010 sec | <= 0.010 sec | 5000V to <50V; FTMS101B |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 360 - 421 °C | 680 - 790 °F | |
| Middle Barrel Temperature | 371 - 421 °C | 700 - 790 °F | |
| Front Barrel Temperature | 382 - 427 °C | 720 - 801 °F | |
| Nozzle Temperature | 377 - 421 °C | 711 - 790 °F | |
| Melt Temperature | 382 - 427 °C | 720 - 801 °F | |
| Mold Temperature | 135 - 163 °C | 275 - 325 °F | |
| Drying Temperature | 149 °C | 300 °F | |
| Dry Time | <= 24 hour | <= 24 hour | |
| Moisture Content | 0.020 % | 0.020 % | Suggested |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 99.9 psi | |
| Clamp Pressure | 41.0 - 69.0 MPa | 5950 - 10000 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | Suggested |
| Vent Depth | 0.00250 - 0.00760 cm | 0.000984 - 0.00299 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |