Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 223 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 223 °C
433 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics EXTEM XH1015 TPI Resin
Thermoplastic Polyimide Extem* XH1015 Resin.
Deflection Temperature at 1.8 MPa (264 psi) 223 °C
433 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics EXTEM XH1015 TPI Resin (Asia Pacific)
Thermoplastic Polyimide Extem* XH1015 Resin.
Deflection Temperature at 1.8 MPa (264 psi) 223 °C
433 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics EXTEM XH1015 TPI Resin (Europe-Africa-Middle East)
Thermoplastic Polyimide Extem* XH1015 Resin.
Deflection Temperature at 1.8 MPa (264 psi) 223 °C
433 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics EXTEM XH1015F TPI Resin (Europe-Africa-Middle East)
Thermoplastic Polyimide Extem* XH1015 Resin. EFSA food Contact approved.
Deflection Temperature at 1.8 MPa (264 psi) 223 °C
433 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP JCL36 PES (Europe-Africa-Middle East)
LNP* LUBRICOMP* JCL36 is a compound based on Polyethersulfone resin containing Carbon Fiber, PTFE. Added features include : Internally Lubricated, Electrically Conductive.
Deflection Temperature at 1.8 MPa (264 psi) 223 °C

@Thickness 3.20 mm
433 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics LNP Thermocomp RFZ71S PA 66
LNP* Thermocomp* RFZ71S is a compound based on Nylon 66 resin containing Glass Fiber, Milled Glass. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for t..
Deflection Temperature at 1.8 MPa (264 psi) 223 °C

@Thickness 3.20 mm
433 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics LNP Thermocomp RFZ71S PA 66 (Asia Pacific)
LNP* Thermocomp* RFZ71S is a compound based on Nylon 66 resin containing Glass Fiber, Milled Glass. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for t..
Deflection Temperature at 1.8 MPa (264 psi) 223 °C

@Thickness 3.20 mm
433 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP VERTON RV00AE PA 66
LNP* VERTON* RV00AE is a compound based on Nylon 66 containing 50% Long Glass Fiber. Added features of this grade include: Easy Molding, Structural.
Deflection Temperature at 1.8 MPa (264 psi) 223 °C
433 °F
ASTM D648
A. Schulman ComAlloy® E-16558 30% Glass Fiber Reinforced Nylon
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 1.8 MPa (264 psi) 223 °C
433 °F
ISO 75-1/-2
Unitika BV2120G15 PA66, 15% Glass Fiber Reinforced, Flame Retardant, Dry
Information provided by Unitika Ltd.
Deflection Temperature at 1.8 MPa (264 psi) >= 223 °C
>= 433 °F
ISO 75 Af
Vyncolit X655RB Glass Fiber and Mineral Filled Novolac Phenolic
Novolac resin based, glass fiber and mineral reinforced. Grade with superior stiffness, high dimensional stability and high wear resistance. Good chemical resistance against several fuels at elevate..
Deflection Temperature at 1.8 MPa (264 psi) 223 °C
433 °F
ASTM D648
A. Schulman ComAlloy® E-16558 30% Glass Fiber Reinforced Nylon
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 1.8 MPa (264 psi) 223 °C
433 °F
ASTM D648
A. Schulman ComAlloy® E-16558 30% Glass Fiber Reinforced Nylon
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 1.8 MPa (264 psi) 223 °C
433 °F
ASTM D648
A. Schulman ComAlloy® E-16558 30% Glass Fiber Reinforced Nylon
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 1.8 MPa (264 psi) 223 °C
433 °F
ASTM D648
A. Schulman ComAlloy® E-16558 30% Glass Fiber Reinforced Nylon
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 1.8 MPa (264 psi) 223 °C
433 °F
ASTM D648
A. Schulman ComAlloy® E-16558 30% Glass Fiber Reinforced Nylon
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 1.8 MPa (264 psi) >= 223 °C
>= 433 °F
ISO 75 Af
Vyncolit BXE7670 Glass Filled Phenolic Molding Compound
Novolac resin based, mainly glass fiber filled. Due to its unique composition, excellent balance between mechanical, thermal and dimensional stability.Information provided by Sumitomo Bak North Ame..
Deflection Temperature at 1.8 MPa (264 psi) 223 °C
433 °F
ASTM Test
BASF Petra® 330 FR BK-112 30% Glass Filled PET
Petra 330 FR BK-112 is a 30% glass reinforced, flame retardant PET, pigmented black injection molding compound rated UL94 V-0 in a 1/64 inch thickness. The product is designed for injection molding..
Deflection Temperature at 1.8 MPa (264 psi) 223 °C

@Thickness 6.35 mm
433 °F

@Thickness 0.250 in
Unannealed; ASTM D648
LNP ULTEM® SMU5831 Polyetherimide, 30% CarbonGlassMineral Reinforced  (discontinued **)
ESD characteristics for ultra high-heat applications. Will be UC3010H.Features: High Heat ResistanceForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Compa..
Deflection Temperature at 1.8 MPa (264 psi) 223 °C

@Thickness 3.20 mm
433 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics LNP Verton WV00A PBT (Europe-Africa-Middle East)
LNP VERTON* WV00A is a compound based on Polybutylene Terephalate resin containing Long Glass.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.