Polymer Property : Tensile Strength at Break = 19000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 131 MPa
19000 psi
ASTM D638
Oxford Polymers 30GF 30% Glass Fiber Filled Polycarbonate for Injection Molding
30% Glass Fiber Filled Polycarbonate for Injection MoldingInformation provided by Oxford Polymers.
Tensile Strength at Break 131 MPa
19000 psi
ASTM D638
Oxford Polymers PBT 30GF PBT, 30% Glass Fiber Reinforced
Product Description: Glass Fiber (30% Reinforced), PBT injection molding grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Release Agents and LubricantsSpecial Characteris..
Tensile Strength at Break 131 MPa
19000 psi
ASTM D638
Oxford Polymers PPS-40GF PPS, 40% Glass Fiber Reinforced
Product Description: Glass Fiber (40% Reinforced), Polyphenylene sulfide injection molding grade Processing and Delivery Form: Pellets and Injection MoldingAppearance: Natural or BlackInformation p..
Tensile Strength at Break 131 MPa
19000 psi
ASTM D638
Polymer Resources NY66-IM-G40 Nylon 66, 40% Glass Reinforced, Impact Modified
Nylon 66, 40% Glass Reinforced, Toughened and LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon g..
Tensile Strength at Break 131 MPa
19000 psi
ASTM D638
Polymer Resources NY6-M25G15 Nylon 6, 25% Mineral, 15% Glass Reinforced
Nylon 6, 25% Mineral, 15% Glass Reinforced, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon gra..
Tensile Strength at Break 131 MPa
19000 psi
ASTM D638
Ravago Manufacturing Americas Hylon® N1040MGL Nylon 6/6 (DAM)  (discontinued **)
Information provided by Ravago.
Tensile Strength at Break 131 MPa
19000 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 2200 PEI (Asia Pacific)
20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification in recognized colors.
Tensile Strength at Break 131 MPa
19000 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem 3451 PEI
45% Glass fiber and mineral filled, standard flow Polyetherimide (Tg 217C) with enhanced dimensional stability. ECO Conforming.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break 131 MPa
19000 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem 3451 PEI (Asia Pacific)
45% Glass fiber and mineral filled, standard flow Polyetherimide (Tg 217C) with enhanced dimensional stability. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break 131 MPa
19000 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM UC1200 PEI (Asia Pacific)
12% carbon fiber reinforced Polyetherimide (Tg 217C). ECO Conforming. UL94 V0 listing in recognized colors.
Tensile Strength at Break 131 MPa
19000 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON Ultem_UC1200 PEI (Europe-Africa-Middle East)
LNP* Stat-kon* Ultem_UC1200 compound is a 12% carbon fiber reinforced PEI. High modulus with ESD characteristics for high-heat applications.
Tensile Strength at Break 131 MPa
19000 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOTUF VF008 PA 66 (Asia Pacific)
LNP THERMOTUF* VF008 is a compound based on Nylon resin containing Glass Fiber. Added features of this material include: High Impact.
Tensile Strength at Break 131 MPa
19000 psi
ASTM D638
SABIC Innovative Plastics LNP VERTON MV00AS PP (Asia Pacific)
LNP VERTON* MV00AS is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled.
Tensile Strength at Break 131 MPa
19000 psi
ASTM D638
SABIC Innovative Plastics LNP STAT-KON RE0029 PA 66
LNP* STAT-KON* RE0029 is a compound based on Nylon 66 resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant.
Tensile Strength at Break 131 MPa
19000 psi
ASTM D638
SABIC Innovative Plastics LNP VERTON MV00ASXP PP (Europe-Africa-Middle East)
LNP VERTON* MV00AS is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled.
Tensile Strength at Break 131 MPa

@Temperature 22.8 °C
19000 psi

@Temperature 73.0 °F
ASTM D638
Ensinger TECATOR™ TI 5031 Polyamide-imide (PAI), Bearing Grade
TECATOR™ is a high performance melt processable polyamideimide that maintains its excellent mechanical and wear properties in temperature environments exceeding 500°F. Stock shapes from Ensinger ..