LNP Stat-Kon® PDX-E-99550 CCS Polyetherimide, Carbon Fiber Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), Carbon Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Stat-Kon® PDX-E-99550 CCS Polyetherimide, Carbon Fiber Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Low to None Ion Content, Electrically ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.37 g/cc
1.37 g/cc
Method A; ASTM D792
Water Absorption 0.20 %
0.20 %
at 24 hrs; ASTM D570
Linear Mold Shrinkage 0.0010 cm/cm
0.0010 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0030 cm/cm
0.0030 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 190 MPa
27600 psi
ASTM D638
Tensile Strength, Yield 190 MPa
27600 psi
ASTM D638
Elongation at Break 1.1 %
1.1 %
ASTM D638
Elongation at Yield 1.1 %
1.1 %
ASTM D638
Tensile Modulus 20.7 GPa
3000 ksi
ASTM D638
Flexural Strength 262 MPa
38000 psi
ASTM D790
Flexural Modulus 18.8 GPa
2730 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Thickness 3.18 mm
1.00 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 3.52 J/cm

@Thickness 3.18 mm
6.59 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 5.30 kJ/m²
2.52 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 24.2 kJ/m²
11.5 ft-lb/in²
ISO 180
Falling Dart Impact 8.50 J
6.27 ft-lb
ASTM D3763
Impact Test 2.63 J
1.94 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear 18.0 µm/m-°C

@Temperature 20.0 °C
10.0 µin/in-°F

@Temperature 68.0 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 22.0 µm/m-°C

@Temperature 20.0 °C
12.2 µin/in-°F

@Temperature 68.0 °F
TMA; ASTM E831
Deflection Temperature at 1.8 MPa (264 psi) 202 °C
396 °F
Unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 0.350 mm
V-0

@Thickness 0.0138 in
Electrical Properties Metric English Comments
Surface Resistance 1.0 - 10000 ohm
1.0 - 10000 ohm
ASTM D4496
Processing Properties Metric English Comments
Melt Temperature 360 - 366 °C
680 - 691 °F
Mold Temperature 121 - 149 °C
250 - 300 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Moisture Content 0.020 %
0.020 %
Suggested
Back Pressure 0.345 - 0.689 MPa
50.0 - 99.9 psi