LG Chemical Lupoy NF1005F 03R Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer LG Chemical
Trade Name LUPOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical Lupoy NF1005F 03R Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: LUPOY NF 1005F03R, eco-friendly UL94 V0/1.5 mm, is designed for extrusion products. It combines an excellent physical property balance of heat resistance, transparency and impact strength and exhibits excellent processing characteristics.Main Characteristics: Good mold release, High viscosity, Non chlorine, bromine, nor phosphate additives and Complying with global environmental standardsApplications: Extrusion application and Information Technology EquipmentCAS: 103598-77-2Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Water Absorption 0.32 %

@Temperature 23.0 °C
0.32 %

@Temperature 73.4 °F
equilibrium, 50% RH; ASTM D570
0.15 %

@Temperature 23.0 °C,
Time 86400 sec
0.15 %

@Temperature 73.4 °F,
Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.00050 - 0.00070 cm/cm
0.00050 - 0.00070 in/in
ASTM D955
Melt Flow 3.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
3.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 73
73
ASTM D785
Tensile Strength, Ultimate 66.0 MPa
9570 psi
ASTM D638
Tensile Strength, Yield 62.0 MPa
8990 psi
50mm/min; ASTM D638
Elongation at Break 120 %
120 %
ASTM D638
Elongation at Yield 6.0 %
6.0 %
ASTM D638
Tensile Modulus 2.20 GPa
319 ksi
ASTM D638
Flexural Yield Strength 90.0 MPa
13100 psi
ASTM D790
Flexural Modulus 2.20 GPa
319 ksi
ASTM D790
Izod Impact, Notched 9.074 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
17.00 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
0.25 mm notch; ASTM D256
Izod Impact, Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ASTM D256
Dart Drop, Total Energy 89.0 J

@Thickness 3.20 mm
65.6 ft-lb

@Thickness 0.126 in
203m/min; ASTM D3763
Abrasion 45

@Load 1.00 kg
45

@Load 2.20 lb
[%], CS-10 F wheel, 500 cycles; ASTM D1044
Thermal Properties Metric English Comments
CTE, linear 68.0 µm/m-°C

@Temperature -40.0 - 82.0 °C
37.8 µin/in-°F

@Temperature -40.0 - 180 °F
ASTM D696
Hot Ball Pressure Test >= 125 °C
>= 257 °F
IEC 598-1
Deflection Temperature at 0.46 MPa (66 psi) 138 °C

@Thickness 4.00 mm
280 °F

@Thickness 0.157 in
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 126 °C

@Thickness 4.00 mm
259 °F

@Thickness 0.157 in
Unannealed; ASTM D648
Vicat Softening Point 147 °C

@Load 5.10 kg
297 °F

@Load 11.2 lb
50°C/hr; ASTM D1525
Softening Point 150 - 200 °C
302 - 392 °F
melting point per MSDS
UL RTI, Electrical 130 °C

@Thickness >=0.750 mm
266 °F

@Thickness >=0.0295 in
130 °C

@Thickness >=1.50 mm
266 °F

@Thickness >=0.0591 in
130 °C

@Thickness >=2.00 mm
266 °F

@Thickness >=0.0787 in
130 °C

@Thickness >=3.00 mm
266 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 110 °C

@Thickness >=0.750 mm
230 °F

@Thickness >=0.0295 in
110 °C

@Thickness >=1.50 mm
230 °F

@Thickness >=0.0591 in
110 °C

@Thickness >=2.00 mm
230 °F

@Thickness >=0.0787 in
110 °C

@Thickness >=3.00 mm
230 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 130 °C

@Thickness >=0.750 mm
266 °F

@Thickness >=0.0295 in
130 °C

@Thickness >=1.50 mm
266 °F

@Thickness >=0.0591 in
130 °C

@Thickness >=2.00 mm
266 °F

@Thickness >=0.0787 in
130 °C

@Thickness >=3.00 mm
266 °F

@Thickness >=0.118 in
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
ASTM D635
V-0

@Thickness 2.00 mm
V-0

@Thickness 0.0787 in
ASTM D635
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
ASTM D635
Flash Point >= 450 °C
>= 842 °F
Oxygen Index 35 %
35 %
ASTM D2863
Glow Wire Test 960 °C

@Thickness 2.00 mm,
Time 5.00 sec
1760 °F

@Thickness 0.0787 in,
Time 0.00139 hour
IEC 695-2-1
Optical Properties Metric English Comments
Refractive Index 1.586
1.586
ASTM D542
Haze 0.70 - 2.0 %
0.70 - 2.0 %
ASTM D1003
Transmission, Visible 89 %
89 %
ASTM D1003
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+17 ohm-cm
2.00e+17 ohm-cm
ASTM D257
Dielectric Constant 3.0

@Frequency 60.0 Hz
3.0

@Frequency 60.0 Hz
ASTM D150
Dielectric Strength 17.0 kV/mm
432 kV/in
ASTM D149
Dissipation Factor 0.0010

@Frequency 60.0 Hz
0.0010

@Frequency 60.0 Hz
ASTM D150
Arc Resistance 0.00 - 60 sec
0.00 - 60 sec
ASTM D495
Comparative Tracking Index 225 V

@Thickness 2.00 mm
225 V

@Thickness 0.0787 in
IEC 112
Hot Wire Ignition, HWI 15 - 30 sec

@Thickness >=2.00 mm
15 - 30 sec

@Thickness >=0.0787 in
15 - 30 sec

@Thickness >=1.50 mm
15 - 30 sec

@Thickness >=0.0591 in
30 - 60 sec

@Thickness >=3.00 mm
30 - 60 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 3.00 mm
>= 120 arcs

@Thickness 0.118 in
>= 120 arcs

@Thickness 2.00 mm
>= 120 arcs

@Thickness 0.0787 in
>= 120 arcs

@Thickness 1.50 mm
>= 120 arcs

@Thickness 0.0591 in
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
Descriptive Properties Value Comments
Autoignition Temperature >450°C