LG Chemical 501S-S HIPS

Category	Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified
Manufacturer	LG Chemical
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LG Chemical 501S-S HIPS.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Self lubricant, Balanced mechanical properties, Good surface appearance with high gloss, Conforming to FDA CFR 177.1640, Excellent processability, Applications include refrigerator food holders, parts of radios and televisions, plastic toys, and yot receptacles

Physical Properties	Metric	English	Comments
Density	1.04 g/cc	0.0376 lb/inÂ³	ASTM D792
Linear Mold Shrinkage	0.0040 - 0.0080 cm/cm	0.0040 - 0.0080 in/in	ASTM D955
Melt Flow	6.0 g/10 min @Load 5.00 kg, Temperature 200 Â°C	6.0 g/10 min @Load 11.0 lb, Temperature 392 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	99	99	ASTM D785
Tensile Strength, Yield	27.5 MPa	3990 psi	50 mm/min; ASTM D638
Elongation at Break	70 %	70 %	50 mm/min; ASTM D638
Flexural Yield Strength	46.2 MPa	6700 psi	15 mm/min; ASTM D790
Flexural Modulus	2.20 GPa	319 ksi	15 mm/min; ASTM D790
Izod Impact, Notched	0.780 J/cm @Thickness 6.35 mm	1.46 ft-lb/in @Thickness 0.250 in	ASTM D256
	1.13 J/cm @Thickness 3.17 mm	2.12 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	79.0 Â°C @Thickness 12.7 mm	174 Â°F @Thickness 0.500 in	Unannealed; ASTM D648
Vicat Softening Point	99.0 Â°C	210 Â°F	1000 g; ASTM D1525
Flammability, UL94	HB	HB	1/8 in
	HB	HB	1/16 in