LATI Latamid 6 H2E04 G/30 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer LATI
Trade Name Latamid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 6 H2E04 G/30 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 6 (PA6) based compound. Heat stabilized. Toughened. Glass fibers. Good elongation.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
Linear Mold Shrinkage, Flow 0.0025 - 0.0050 cm/cm
0.0025 - 0.0050 in/in
Linear Mold Shrinkage, Transverse 0.0055 - 0.0075 cm/cm
0.0055 - 0.0075 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.0 MPa

@Temperature 150 °C
 9430 psi

@Temperature 302 °F
75.0 MPa

@Temperature 120 °C
 10900 psi

@Temperature 248 °F
90.0 MPa

@Temperature 90.0 °C
 13100 psi

@Temperature 194 °F
115 MPa

@Temperature 60.0 °C
 16700 psi

@Temperature 140 °F
150 MPa

@Temperature 23.0 °C
 21800 psi

@Temperature 73.4 °F
Elongation at Break 3.5 %

@Temperature 23.0 °C
 3.5 %

@Temperature 73.4 °F
4.8 %

@Temperature 60.0 °C
 4.8 %

@Temperature 140 °F
6.4 %

@Temperature 90.0 °C
 6.4 %

@Temperature 194 °F
6.9 %

@Temperature 120 °C
 6.9 %

@Temperature 248 °F
8.0 %

@Temperature 150 °C
 8.0 %

@Temperature 302 °F
Elongation at Yield 4.6 %

@Temperature 60.0 °C
 4.6 %

@Temperature 140 °F
6.1 %

@Temperature 90.0 °C
 6.1 %

@Temperature 194 °F
6.8 %

@Temperature 120 °C
 6.8 %

@Temperature 248 °F
7.6 %

@Temperature 150 °C
 7.6 %

@Temperature 302 °F
Tensile Modulus 2.90 GPa

@Temperature 150 °C
 421 ksi

@Temperature 302 °F
3.60 GPa

@Temperature 120 °C
 522 ksi

@Temperature 248 °F
4.40 GPa

@Temperature 90.0 °C
 638 ksi

@Temperature 194 °F
6.70 GPa

@Temperature 60.0 °C
 972 ksi

@Temperature 140 °F
8.30 GPa

@Temperature 23.0 °C
 1200 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched NB
NB
Charpy Impact, Notched 8.00 J/cm²
38.1 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 100 °C
212 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
Vicat Softening Point 215 °C

@Load 5.00 kg
 419 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa