Kingfa PA66-R0N Flame Retardant PA66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant
Manufacturer Kingfa Sci. & Tech. Co.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kingfa PA66-R0N Flame Retardant PA66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features:Flame retardantHigh strengthHigh temperature propertiesGood electric propertiesNo bloomingApplications:Injection moldingConnectorsRelay, bobbins, plugsHousehold appliance partsE & E partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.25 g/cc

@Temperature 23.0 °C
 1.25 g/cc

@Temperature 73.4 °F
 ASTM D792
Water Absorption 0.60 %

@Temperature 23.0 °C,
Time 86400 sec
 0.60 %

@Temperature 73.4 °F,
Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage 0.013 - 0.015 cm/cm

@Temperature 23.0 °C
 0.013 - 0.015 in/in

@Temperature 73.4 °F
 ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 112
112
ASTM D785
Tensile Strength at Break 50.0 MPa
7250 psi
10mm/min; ASTM D638
Elongation at Break >= 25 %
>= 25 %
10mm/min; ASTM D638
Flexural Strength 74.0 MPa
10700 psi
2mm/min; ASTM D790
Flexural Modulus 2.15 GPa
312 ksi
2mm/min; ASTM D790
Izod Impact, Notched 0.850 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 1.59 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 242 °C

@Thickness 6.40 mm
 468 °F

@Thickness 0.252 in
 ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C

@Thickness 6.40 mm
 149 °F

@Thickness 0.252 in
 ASTM D648
Flammability, UL94 V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Processing Temperature <= 310 °C
<= 590 °F
Rear Barrel Temperature 255 - 275 °C
491 - 527 °F
Start Point: 265°C
Middle Barrel Temperature 260 - 290 °C
500 - 554 °F
Start Point: 280°C
Front Barrel Temperature 270 - 300 °C
518 - 572 °F
Start Point: 285°C
Melt Temperature 275 - 300 °C
527 - 572 °F
Start Point: 285°C
Mold Temperature 50.0 - 70.0 °C
122 - 158 °F
Start Point: 60°C
Drying Temperature 90.0 - 110 °C

@Time 14400 - 21600 sec
 194 - 230 °F

@Time 4.00 - 6.00 hour
 Pre-dry
Descriptive Properties Value Comments
Injection Speed Moderate to High