- Honeywell Capran® Emblem™ 1200MT Bi-Axially Oriented Nylon Film
Honeywell Capran® Emblem™ 1200MT Bi-Axially Oriented Nylon Film
| Category | Polymer , Film , Thermoplastic , Nylon |
| Manufacturer | Honeywell |
| Trade Name | Capran® Emblem™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell Capran® Emblem™ 1200MT Bi-Axially Oriented Nylon Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Capran® Emblem™ 1200MT is a bi-axially oriented nylon film. It is a versatile and robust film that satisfies many packaging needs, and has superior resistance to oils, fats, hydrocarbons, and many solvents. It is also microwavable, making it an excellent choice for lidding stock. 1200MT film has a metallized coating that provides an effective barrier to oxygen, helium, and water vapor. Applications: message balloons as well as food packaging requiring high barrier. Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0420 lb/in³ | Yield Density |
| Water Vapor Transmission | 2.64 g/m²/day | 0.170 g/100 in²/day | 100°F / 100%RH); ASTM F1249 |
| Oxygen Transmission Rate | 1.086 cc/m²/day | 0.06994 cc/100 in²/day | 77°F / 0% / RH; ASTM D3985 |
| Thickness | 12.2 microns | 0.480 mil |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 60 - 90 % | 60 - 90 % | ASTM D882 |
| Film Elongation at Break, TD | 60 - 90 % | 60 - 90 % | ASTM D882 |
| Secant Modulus, MD | 2.41 - 3.93 GPa | 350 - 570 ksi | ASTM D882 |
| Secant Modulus, TD | 2.482 - 3.59 GPa | 360.0 - 521 ksi | ASTM D882 |
| Coefficient of Friction | 0.17 - 0.28 | 0.17 - 0.28 | film to stainless steel; ASTM D1894 |
| 0.55 - 0.74 | 0.55 - 0.74 | film to film; ASTM D1894 | |
| Tear Strength Test | 1100 - 1500 | 1100 - 1500 | graves tear, grams/mil (initial); ASTM D1004 |
| Elmendorf Tear Strength, MD | 0.4102 - 0.6563 g/micron | 10.42 - 16.67 g/mil | |
| Film Tensile Strength at Break, MD | 193 - 276 MPa | 28000 - 40000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 193 - 276 MPa | 28000 - 40000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 1.6 - 2.5 % | 1.6 - 2.5 % | 320°F / 160°C - 5 minutes; ASTM D1204 |
| Shrinkage, TD | 0.20 - 0.70 % | 0.20 - 0.70 % | 320°F / 160°C - 5 minutes; ASTM D1204 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Helium Transition Rate | max 6 cc/100 in2/day | ASTM 1434 |