Polymer Property : Film Tensile Strength at Break, MD = 193 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Film Tensile Strength at Break, MD 193 - 276 MPa
28000 - 40000 psi
ASTM D882
Honeywell Capran® Emblem™ 1200Matte Matte Coated Bi-Axially Oriented Nylon Film
Description: Capran® Emblem™ 1200Matte is a bi-axially oriented nylon film. It is a versatile and robust film that satisfies many packaging needs, and has superior resistance to oils, fats,..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Melinex® 1311 Polyester Film
Melinex® 1311 is a clear polyester film with antistatic properties on both surfaces for improved web handling and safety.Information provided by DuPont.
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Melinex® 314 Polyester Film, 200 Gauge
Melinex® 314 is a two-side adhesion promoting polyester film with consistently good handling properties.Information provided by DuPont.
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Melinex® 314 Polyester Film, 92 Gauge
Melinex® 314 is a two-side adhesion promoting polyester film with consistently good handling properties.Information provided by DuPont.
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Melinex® 453 Polyester Film, 142 Gauge
Melinex® 453 is an excellent handling, high clarity film with one side pre-treated to promote adhesion to most printing inks and Industrial coatings.Typical Applications: Melinex® 453 is used as a..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Melinex® 453 Polyester Film, 200 Gauge
Melinex® 453 is an excellent handling, high clarity film with one side pre-treated to promote adhesion to most printing inks and Industrial coatings.Typical Applications: Melinex® 453 is used as a..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Melinex® 453 Polyester Film, 400 Gauge
Melinex® 453 is an excellent handling, high clarity film with one side pre-treated to promote adhesion to most printing inks and Industrial coatings.Typical Applications: Melinex® 453 is used as a..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Melinex® 453 Polyester Film, 700 Gauge
Melinex® 453 is an excellent handling, high clarity film with one side pre-treated to promote adhesion to most printing inks and Industrial coatings.Typical Applications: Melinex® 453 is used as a..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Melinex® 454 Polyester Film, 500 Gauge
Melinex® 454 is an excellent handling, high clarity film with both sides pre-treated to promote adhesion to most printing inks and Industrial coatings.Typical Applications: Melinex® 454 is used as..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Melinex® 454 Polyester Film, 700 Gauge
Melinex® 454 is an excellent handling, high clarity film with both sides pre-treated to promote adhesion to most printing inks and Industrial coatings.Typical Applications: Melinex® 454 is used as..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Melinex® 455 Polyester Film
Melinex® 455 is a high clarity polyester film pretreated on one side for slip. It has excellent handling characteristics.General Product Info: Two smooth coatable surfacesLow surface resistivityCan..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Melinex® 456 Polyester Film
Melinex® 456 is an excellent handling, high clarity polyester film with both sides pretreated for slip. The two smooth surfaces allow easy top coating.Approvals: UL 94 VTM-2 - for 200 - 700 gauge (..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Melinex® 581 Polyester Film
A super clear, one side C-Sub pretreated film for adhesion of hydrophilic coatings.Approvals: UL Recognition - Product has been registered with Underwriters LaboratoriesInformation provided by DuPon..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Melinex® SWC Polyester Film, 200 Gauge
A narrow width film with consistently good handling properties; transparent in thin gauges, slightly hazy in thick gauges, ideally suited for wire and cable wrapping and insulation.Information provi..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Melinex® SWC Polyester Film, 400 Gauge
A narrow width film with consistently good handling properties; transparent in thin gauges, slightly hazy in thick gauges, ideally suited for wire and cable wrapping and insulation.Information provi..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Melinex® SWC Polyester Film, 48 Gauge
A narrow width film with consistently good handling properties; transparent in thin gauges, slightly hazy in thick gauges, ideally suited for wire and cable wrapping and insulation.Information provi..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Mylar® A Polyester Film, 200 Gauge
Mylar® A films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion, ..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Mylar® A Polyester Film, 75 Gauge
Mylar® A films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion, ..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Mylar® DS Polyester Film
Mylar® DS is a super clear, biaxially oriented, polyester film with differential surface roughness on each side. Its unique composition, consisting of a smooth side opposite a rougher, filled side,..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Mylar® EL Polyester Film, 142 Gauge
Mylar® EL films, typically 48 through 500 gauge are strong, tough, general -purpose films for electrical/electronic uses. Heavier gauges of Mylar® EL films are similar to Mylar® MO films. Availab..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Mylar® EL Polyester Film, 92 Gauge
Mylar® EL films, typically 48 through 500 gauge are strong, tough, general -purpose films for electrical/electronic uses. Heavier gauges of Mylar® EL films are similar to Mylar® MO films. Availab..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Mylar® MDA Polyester Film, 75 Gauge
Mylar® MDA films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Mylar® RSX951 Polyester Film, 140 Gauge
Mylar® RSX951 is a silicone coated polyester film designed for use as a release liner in various casting applications. The silicone release coating is applied to the film during the film production..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Mylar® RSX951 Polyester Film, 175 Gauge
Mylar® RSX951 is a silicone coated polyester film designed for use as a release liner in various casting applications. The silicone release coating is applied to the film during the film production..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Teijin® Tetoron® SLA Polyester Film, 500 Gauge
Teijin® Tetoron® SLA is a super low shrinkage version of Teijin® Tetoron® type S polyester film. In addition to having the well balanced physical, chemical and electrical properties of type S fi..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Mylar® HR951 Polyester Film, 92 Gauge
Mylar® HR951 is a one-side release coated polyester film with good handling properties and clarity. It has been developed for use in various industrial applications.Information provided by DuPont.
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Mylar® WC Polyester Film, 142 Gauge
Mylar® WC films are general-purpose electrical grade films, similar to Mylar® EL. These clear to hazy films are tough and durable as a core wrap. They offer good dielectrics and good handling char..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Mylar® WC Polyester Film, 75 Gauge
Mylar® WC films are general-purpose electrical grade films, similar to Mylar® EL. These clear to hazy films are tough and durable as a core wrap. They offer good dielectrics and good handling char..
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Melinex® 516R Polyester Film
A high clarity film which is two side pretreated for slip to combine good handling properties with high clarity and brillianceInformation provided by DuPont.
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
DuPont Teijin Films Melinex® 457 Polyester Film, 200 Gauge
Melinex® 457 is one side slip, one side adhesion promoting, super clear, polyester film for color proof applications.Also available in 650 gaugeInformation provided by DuPont.