Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, TD | 193 - 303 MPa | 28000 - 44000 psi | ASTM D882 |
Honeywell Capran® Emblem™ 1230 Bi-Axially Oriented Nylon Film
(discontinued **) Description: Capran® Emblem™ 1230 is a bi-axially oriented nylon film. It is a versatile and robust film that satisfies many packaging needs, and has superior resistance to oils, fats, hydrocarbo.. |
|||
Film Tensile Strength at Break, TD | 193 - 303 MPa | 28000 - 44000 psi | ASTM D882 |
Honeywell Capran® Emblem™ 1200 Bi-Axially Oriented Nylon Film Description: Capran® Emblem™ 1200 is a bi-axially oriented nylon film. It is a versatile and robust film that satisfies many packaging needs, and has superior resistance to oils, fats, hydr.. |
|||
Film Tensile Strength at Break, TD | 193 - 303 MPa | 28000 - 44000 psi | ASTM D882 |
Honeywell Capran® Emblem™ 1200M Bi-Axially Oriented Nylon 6 Film Description: Capran® Emblem™ 1200M is a 0.48 mil (12 micron) biaxially oriented nylon 6 film with a polymeric coating which provides enhanced adhesion to a variety of inks, coatings, and adh.. |
|||
Film Tensile Strength at Break, TD | 193 - 276 MPa | 28000 - 40000 psi | ASTM D882 |
Honeywell Capran® Emblem™ 1200Matte Matte Coated Bi-Axially Oriented Nylon Film Description: Capran® Emblem™ 1200Matte is a bi-axially oriented nylon film. It is a versatile and robust film that satisfies many packaging needs, and has superior resistance to oils, fats,.. |
|||
Film Tensile Strength at Break, TD | 193 - 276 MPa | 28000 - 40000 psi | ASTM D882 |
Honeywell Capran® Emblem™ 1200MT Bi-Axially Oriented Nylon Film Description: Capran® Emblem™ 1200MT is a bi-axially oriented nylon film. It is a versatile and robust film that satisfies many packaging needs, and has superior resistance to oils, fats, hy.. |
|||
Film Tensile Strength at Break, TD | 193 - 303 MPa | 28000 - 44000 psi | ASTM D882 |
Honeywell Capran® Emblem™ 1500M M-Coated Bi-Axially Oriented Nylon Film Description: Capran® Emblem™ 1500M is a bi-axially oriented nylon film. It is a versatile and robust film that satisfies many packaging needs, and has superior resistance to oils, fats, hyd.. |
|||
Film Tensile Strength at Break, TD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 301H Polyester Film Melinex® 301H is a coextruded film that is one side heat sealable and is able to accept many industrial coatings.Information provided by DuPont. |
|||
Film Tensile Strength at Break, TD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 623 Polyester Film, 700 Gauge Melinex® 623 is a super clear polyester film pretreated on both surfaces to give superior solvent adhesion and improved handleability.Information provided by DuPont. |
|||
Film Tensile Strength at Break, TD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 623 Polyester Film, 750 Gauge Melinex® 623 is a super clear polyester film pretreated on both surfaces to give superior solvent adhesion and improved handleability.Information provided by DuPont. |
|||
Film Tensile Strength at Break, TD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 680 Polyester Film, 750 Gauge Melinex® 680 is a super clear polyester film, pretreated on one side to promote adhesion with improved handleability. It is high clarity, non-yellow base with excellent adhesion on the pretreated s.. |
|||
Film Tensile Strength at Break, TD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 680 Polyester Film, 700 Gauge Melinex® 680 is a super clear polyester film, pretreated on one side to promote adhesion with improved handleability. It is high clarity, non-yellow base with excellent adhesion on the pretreated s.. |
|||
Film Tensile Strength at Break, TD | 193 MPa | 28000 psi | ASTM D882 |
DuPont Teijin Films Mylar® MC2 Polyester Film, 50 Gauge (14 µm), PVDC Coated Data provided by DuPont Packaging Polymers.A polyester film with a vacuum deposited layer of aluminum on one side and overcoated on both sides with a heat sealable PVDC copolymer. The film has exce.. |