Gromax BFG30-FU03B3 Nylon 6 32.9% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BFG30-FU03B3 Nylon 6 32.9% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ISO 1183 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Melt Flow | 41.1 g/10 min @Load 5.00 kg, Temperature 275 °C |
41.1 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 164.9 MPa | 23920 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 3.2 % | 3.2 % | 50 mm/min; ISO 527 |
| Flexural Strength | 263 MPa | 38100 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 9.75 GPa | 1410 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 117.4 kJ/m² | 55.86 ft-lb/in² | ISO 180-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 209.1 °C | 408.4 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 265 - 280 °C | 509 - 536 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- LG Chemical LUMID GP2500B(W) PA66+GF50%, General Purpose
- Lucite International Elvacite ® 2046 Acrylic Resin
- Chevron Phillips EC6600 HIPS - High Impact Polystyrene
- Chosun Refractories HSC-17 Dense and High-Strength Castable, Credens
- Braskem Evateno® HM 728 EVA Hot Melt Copolymer
- Braskem LL 218/21 LLDPE Blown Film Extrusion Polyethylene
- Arlon 55579R033 0.033" (0.838 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Ashley Polymers Ashlene® RH190TB Acetal
- Radici Radilon® A RV330 (dry) Nylon 66
Copyright © lookpolymers.com All Rights Reserved