DuPont Teijin Films Mylar® RL43 Polyester Packaging Film, 50 Gauge

Category Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer DuPont Teijin Films (DTF)
Trade Name Mylar®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Teijin Films Mylar® RL43 Polyester Packaging Film, 50 Gauge.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by DuPont Packaging Polymers.Mylar® RL43 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. Mylar® RL43 is designed to produce strong heat seals to polypropylene (PP). Although designed especially to seal to polypropylene, Mylar® RL43 will produce strong seals to a broad range of container substrates including amorphous polyester (APET, also PETG), semicrystalline polyester (CPET), polyester coated paperboard, polyvinylchloride (PVC), polyethylene (HDPE), and polystyrene (HIPS). Mylar® RL43 has the same type heat seal layer as Mylar® RL42, but the seal layer is thicker than Mylar® RL42. Mylar® RL43 produces the highest seal strengths to polypropylene of Mylar® lidding films and tends to produce tearing seals to non-polar substrates under chilled conditions. Mylar® RL43 is recommended when light caulking is needed. Mylar® RL43, like other RL types, has a lower seal initiation temperature than lidding films with an amorphous polyester heat seal layer (e.g., Mylar® OL, OL2). This allows good seals to be made at higher line speeds (or using lower sealing temperatures).
Physical Properties Metric English Comments
Density 1.25 g/cc
0.0452 lb/in³
Calculated from nominal thickness and yield
Moisture Vapor Transmission 0.980 cc-mm/m²-24hr-atm
2.49 cc-mil/100 in²-24hr-atm
Proc. E; ASTM E96
Oxygen Transmission 3.15 cc-mm/m²-24hr-atm
8.00 cc-mil/100 in²-24hr-atm
Tested per ASTM D3985 at 22°C
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 110 %
110 %
ASTM D882
Film Elongation at Break, TD 80 %
80 %
ASTM D882
Secant Modulus 3.79 GPa
550 ksi
Stiffness Modulus; ASTM D882
Tear Strength Test 0.70
0.70
lb Graves; ASTM D1004
Film Tensile Strength at Break, MD 172 MPa
24900 psi
ASTM D882
Film Tensile Strength at Break, TD 241 MPa
35000 psi
ASTM D882
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Minimum Service Temperature, Air -40.0 °C
-40.0 °F