Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
Total PPH 3271 Polypropylene, Oriented Film Extrusion Grade Homopolymer film gradeLow Residuals – FINA 3271 utilizes the new Fina proprietary process technology to provide extremely low residuals for improved color stability and clarity.Slip/Antiblock –.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor® 75 SLP OPP Film Product Description: Bicor SLP is a one-side treated, non-heat sealable OPP film designed for use as the outside web of a lamination. The treated print surface is intended as the print and laminatin.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor™ 60 SLP OPP Film Product Description: Bicor SLP is a one-side treated, non-heat sealable OPP film designed for use as the outside web of a lamination. The treated print surface is intended as the print and laminatin.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Label-Lyte® 25 LLG-101 Clear OPP Film Product Description: A clear, one-side treated, biaxially oriented polypropylene film that is used in roll-fed labeling. This film can be laminated to itself (at other gauges of LLG-101) or applied .. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Label-Lyte™ 25LL-101 OPP Film Product Description: A clear, one-side treated, polypropylene film that is designed to provide exceptional clarity and print protection when used as overlaminates in pressure-sensitive labeling appl.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 437 Polyester Film, 200 Gauge Melinex® 437 is a two side differentially pretreated super clear film; 1 side promotes adhesion, 1 side slip.Also available in 270, 370, 465, 650 GaugeInformation provided by DuPont. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 583 Polyester Film, 300 Gauge Melinex® 583 is a high clarity, differentially treated polyester film. One side is hydrophilic pretreated to promote adhesion to many industrial aqueous coatings and inks, and the opposite side is .. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® OB01 Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® OB01 (formerly known as XM924) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and a polyvinylidene chlor.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
DuPont Teijin Films Mylar® OB13AF Polyester Film, 150 Gauge Product Description: Mylar® OB13AF is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer on one side and a polyvinylidene chloride (PVdC) layer on the opposite s.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® OL13 Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® OL13 (formerly known as XM110) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer. It is used as a heat seal.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® OL13 Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® OL13 (formerly known as XM110) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer. It is used as a heat seal.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
DuPont Teijin Films Mylar® OL2 Polyester Film, 100 Gauge Product Description: Mylar® OL2 is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer. It is used as a heat sealable lidding film in packaging refrigerated and f.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
DuPont Teijin Films Mylar® OL2 Polyester Film, 75 Gauge Product Description: Mylar® OL2 is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer. It is used as a heat sealable lidding film in packaging refrigerated and f.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RB42AF Polyester Film, 100 Gauge Product Description: Mylar® RB42AF is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer and polyvinylidene chloride (PVdC) layer on the opposite side. .. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RL31 Polyester Film, 100 Gauge Mylar® RL31 is a biaxially oriented polyester (OPET) with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a heat sealable lidding film in packaging frozen and refrigerated foods. Myl.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL32 Polyester Packaging Film, 150 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL32 (formerly known as XM999) is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a .. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL4 Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL4 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a heat sealable lidding film .. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL4 Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL4 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a heat sealable lidding film .. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL4 Polyester Packaging Film, 75 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL4 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a heat sealable lidding film .. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL42 Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL42 (formerly known as XM985) is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a .. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL42 Polyester Packaging Film, 75 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL42 (formerly known as XM985) is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a .. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL43 Polyester Packaging Film, 150 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL43 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. Mylar® RL43 is designed to produce stro.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL43 Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL43 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. Mylar® RL43 is designed to produce stro.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ExxonMobil Method |
ExxonMobil Bicor® 110 ASB-X OPP Film Product Description: Bicor ASB-X is a two side coated, sealable OPP film designed for broad use in many applications, including overwrap, horizontal, and vertical packaging. ASB-X is good for heavy .. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor® 120 CSR-2 OPP Film Product Description: Bicor CSR-2 is a one-side treated OPP film designed for cold seal release, either unsupported or as the outer web of a lamination.Availability: Latin America, North America and .. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor® 120 SLP OPP Film Product Description: Bicor SLP is a one-side treated, non-heat sealable OPP film designed for use as the outside web of a lamination. The treated print surface is intended as the print and laminatin.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® OB12 Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® OB12 is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and polyvinylidene chloride (PVDC) layer on the oppo.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® OB12AF Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® OB12AF is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and polyvinylidene chloride (PVDC) layer on the op.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 516R Polyester Film A high clarity film which is two side pretreated for slip to combine good handling properties with high clarity and brillianceInformation provided by DuPont. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® LBT-2 Polyester Packaging Film, 75 Gauge Data provided by DuPont Packaging Polymers.Mylar® LBT-2 is an uncoated, transparent, exceptionally strong film used as a substrate for laminating and extrusion coating and as a component of packagi.. |