Cresset Powers Cress-Alon™ NE2740 4% Nano Clay Loaded, 2.7 r.v. Compounding Grade Nylon 6, 50% RH

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer Cresset Powers, Ltd
Trade Name Cress-Alon™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Cresset Powers Cress-Alon™ NE2740 4% Nano Clay Loaded, 2.7 r.v. Compounding Grade Nylon 6, 50% RH.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Low density, high rigidity, high heat distortion temperature, high retention of mechanical properties under humid conditions, flame retardant, recyclable and environmentally friendly, less glass fiber required to achieve same properties as non-nano nylon, low opacifying property, excellent surface smoothness and glossiness, low water absorption, excellent moldability, high crystallinity, good dimensional stability, good barrier properties to gas, solvent, and UV, high resistance to oil, greases, hydrocarbons, and chemicals, and may help flame retardant properties with anti-dripping.Information provided by Cresset Powers Ltd.
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
ASTM D792
Viscosity Measurement 2.7
2.7
Relative Viscosity
Melt Flow 48.3 g/10 min

@Load 5.00 kg,
Temperature 235 °C
48.3 g/10 min

@Load 11.0 lb,
Temperature 455 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 96.0 MPa
13900 psi
ASTM D638
Tensile Strength, Yield 96.0 MPa
13900 psi
ASTM D638
Elongation at Break 2.3 %
2.3 %
ASTM D638
Elongation at Yield 2.4 %
2.4 %
ASTM D638
Flexural Yield Strength 143 MPa
20700 psi
ASTM D790
Flexural Modulus 3.70 GPa
537 ksi
ASTM D790
Izod Impact, Notched 0.380 J/cm
0.712 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Melting Point 221 °C
430 °F
ASTM DSC