Bulk Molding Compounds BMC 680 Mineral Filled, Glass Fiber Reinforced Polyester Compound

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Polyester, TS , Thermoset Polyester Glass and Mineral Filled BMC
Manufacturer	BMC - Bulk Molding Compounds Inc.
Trade Name	BMC
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Bulk Molding Compounds BMC 680 Mineral Filled, Glass Fiber Reinforced Polyester Compound.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

BMC 680 molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression and stuffer injection molding It is characterized by good moldability, very high impact strength, oil and solvent resistance and creep resistance at elevated temperatures.Typical applications include replacements for die castings and sheet molding compounds, valve covers, intake manifolds, oil pans and circuit breakers.

Physical Properties	Metric	English	Comments
Specific Gravity	1.71 g/cc	1.71 g/cc
Water Absorption	0.15 %	0.15 %	24 hours, 23°C
Linear Mold Shrinkage	0.0010 - 0.0020 cm/cm	0.0010 - 0.0020 in/in

Mechanical Properties	Metric	English
Hardness, Barcol	50 - 60	50 - 60
Tensile Strength, Ultimate	96.5 - 117 MPa	14000 - 17000 psi
Flexural Strength	207 - 241 MPa	30000 - 35000 psi
Compressive Strength	131 - 165 MPa	19000 - 24000 psi
Izod Impact, Notched	11.2 - 13.9 J/cm	21.0 - 26.0 ft-lb/in

Thermal Properties	Metric	English
Deflection Temperature at 1.8 MPa (264 psi)	>= 260 °C	>= 500 °F
Flammability, UL94	HB @Thickness 3.17 mm	HB @Thickness 0.125 in
	HB @Thickness 1.59 mm	HB @Thickness 0.0625 in
	V-0 @Thickness 6.35 mm	V-0 @Thickness 0.250 in

Electrical Properties	Metric	English	Comments
Dielectric Strength	15.0 - 15.7 kV/mm	380 - 400 kV/in	Short Time
Arc Resistance	>= 180 sec	>= 180 sec
Comparative Tracking Index	>= 600 V	>= 600 V

Processing Properties	Metric	English	Comments
Mold Temperature	138 - 166 °C	280 - 330 °F