Bhansali Engineering Santron IMS 2000 SAN Resin
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Bhansali Engineering Santron IMS 2000 SAN Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Clear SANInformation provided by Bhansali
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.00400 - 0.00500 cm/cm | 0.00400 - 0.00500 in/in | ASTM D955 |
| Melt Flow | 35.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
35.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Yield | 63.7 MPa @Thickness 3.20 mm |
9250 psi @Thickness 0.126 in |
Type I, 5 mm/min; ASTM D638 |
| 68.6 MPa @Thickness 3.20 mm |
9960 psi @Thickness 0.126 in |
Type I, 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 98.1 MPa @Thickness 6.40 mm |
14200 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.294 J/cm @Thickness 3.20 mm |
0.551 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C @Thickness 6.40 mm |
203 °F @Thickness 0.252 in |
Method A; ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |
Users viewing this material also viewed the following:
- PTS Trilac® FR1 ABS- Flame Retardant ABS Resin (Unverified Data**)
- Hong Kun Group 3-Bromo-2-methylbenzoic Acid Pharmaceutical Intermediate
- Taiwan Sheen Soon Sheenthane® A8970A Film Grade Thermoplastic Polyurethane Elastomer
- Borealis Borpact™ SG321MO Polypropylene Random Heterophasic Copolymer for Injection Molding
- Zotefoams Evazote® VA25 Ethylene Vinyl Acetate Copolymer Foam
- Arkema Group Rilsan® BESHV Nylon 11, Blow Molding Grade (Dry)
- AKG Polymers Vision PP PPH BL1302 T20 Polypropylene Compound
- Aremco Ceramabind™ 880 High Temperature Inorganic Binder
- PlastxWorld CEVIAN®-V 320 ABS
Copyright © lookpolymers.com All Rights Reserved