Polymer Property : Tensile Strength, Yield = 9960 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	68.6 MPa @Thickness 3.20 mm	9960 psi @Thickness 0.126 in	Type I, 50 mm/min; ASTM D638
Bhansali Engineering Santron IMS 2000 Glitter SAN Resin High Transparent SANInformation provided by Bhansali
Tensile Strength, Yield	68.6 MPa @Thickness 3.20 mm	9960 psi @Thickness 0.126 in	Type I, 50 mm/min; ASTM D638
Bhansali Engineering Santron IMS 2000 SAN Resin Clear SANInformation provided by Bhansali
Tensile Strength, Yield	68.6 MPa @Thickness 3.20 mm	9960 psi @Thickness 0.126 in	Type I, 5 mm/min; ASTM D638
Bhansali Engineering Santron IMS 2007LF SAN Resin High Rigidity Clear SANInformation provided by Bhansali
Tensile Strength, Yield	68.6 MPa @Thickness 3.20 mm	9960 psi @Thickness 0.126 in	Type I, 50 mm/min; ASTM D638
Bhansali Engineering Santron IMS1000 Sparkle SAN Resin High Transparent SANInformation provided by Bhansali
Tensile Strength, Yield	68.6 MPa @Thickness 3.20 mm	9960 psi @Thickness 0.126 in	Type I, 50 mm/min; ASTM D638
Bhansali Engineering Santron IMS 2000 SAN Resin Clear SANInformation provided by Bhansali
Tensile Strength, Yield	68.6 MPa @Thickness 3.20 mm	9960 psi @Thickness 0.126 in	Type I, 5 mm/min; ASTM D638
Bhansali Engineering Santron IMS 2007LF SAN Resin High Rigidity Clear SANInformation provided by Bhansali
Tensile Strength, Yield	68.6 MPa @Thickness 3.20 mm	9960 psi @Thickness 0.126 in	Type I, 50 mm/min; ASTM D638
Bhansali Engineering Santron IMS1000M SAN Resin Clear SAN, Pen barrel applicationInformation provided by Bhansali
Tensile Strength, Yield	68.6 MPa @Thickness 3.20 mm	9960 psi @Thickness 0.126 in	Type I, 50 mm/min; ASTM D638
Bhansali Engineering Santron IMS 2000 Glitter SAN Resin High Transparent SANInformation provided by Bhansali
Tensile Strength, Yield	68.6 MPa @Thickness 3.20 mm	9960 psi @Thickness 0.126 in	Type I, 50 mm/min; ASTM D638
Bhansali Engineering Santron IMS1000 SAN Resin Clear SANInformation provided by Bhansali
Tensile Strength, Yield	68.6 MPa @Thickness 3.20 mm	9960 psi @Thickness 0.126 in	Type I, 50 mm/min; ASTM D638
Bhansali Engineering Santron IMS1000M SAN Resin Clear SAN, Pen barrel applicationInformation provided by Bhansali
Tensile Strength, Yield	68.6 MPa @Thickness 3.20 mm	9960 psi @Thickness 0.126 in	Type I, 50 mm/min; ASTM D638
Bhansali Engineering Santron IMS1000 SAN Resin Clear SANInformation provided by Bhansali
Tensile Strength, Yield	68.6 MPa @Thickness 3.20 mm	9960 psi @Thickness 0.126 in	Type I, 50 mm/min; ASTM D638
Bhansali Engineering Santron IMS1000 Sparkle SAN Resin High Transparent SANInformation provided by Bhansali