BASF Ultramid® 8231G HS BK-106 14% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8231G HS BK-106 14% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8231G HS BK-106 is a black pigmented heat stabilized, 14% glass fiber reinforced PA6 injection molding compound.The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and ydrocarbons.
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
ISO 1183
Water Absorption 1.4 %
1.4 %
24 hour; ISO Test
8.1 %
8.1 %
ISO 62
Moisture Absorption at Equilibrium 2.3 %
2.3 %
23°C/50% R.H.; ISO 62
Viscosity Measurement 50
50
Formic Acid
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM Test
Tensile Strength at Break 118 MPa
17100 psi
0.2 in/min; ASTM Test
Tensile Strength, Ultimate 118 MPa
17100 psi
5mm/min; ISO 527
Elongation at Break 2.9 %
2.9 %
0.2 in/min; ASTM Test
Flexural Modulus 4.94 GPa
716 ksi
ASTM Test
5.10 GPa
740 ksi
ISO Data
Izod Impact, Notched 0.430 J/cm

@Thickness 3.17 mm
0.806 ft-lb/in

@Thickness 0.125 in
ASTM Test
Izod Impact, Notched (ISO) 3.80 kJ/m²
1.81 ft-lb/in²
ISO Test
Thermal Properties Metric English Comments
CTE, linear 50.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
27.8 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 1.8 MPa (264 psi) 199 °C
390 °F
ISO 75
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Descriptive Properties Value Comments
Color BK-106
Commercial Status Active America
Impact Modified No
Primary Processing Technique Injection Molding
UL.UL-C Yes
Copyright © lookpolymers.com All Rights Reserved