Polymer Property : Tensile Strength, Ultimate = 17100 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	118 MPa	17100 psi	DIN 53455; ASTM D638
Kolon KOPAÂ® KN132G15VO G/F Reinforced Flame Retardant Nylon 6 KOPAÂ® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr..
Tensile Strength, Ultimate	118 MPa	17100 psi	DIN 53455; ASTM D638
Kolon KOPAÂ® KN135HB30HI Multi Reinforced Nylon 6 KOPAÂ® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr..
Tensile Strength, Ultimate	118 MPa	17100 psi
Shinil Chemical SHINFLAME PC/PBT GF Flame Retardant Polymer Appliance SHINFLAME is a flame retardant (FR) compound which exhibits inherent flame retardant properties during fire. Shinil uses its patented dispersion blending technology with variety of polymers to prod..
Tensile Strength, Ultimate	118 MPa	17100 psi	ISO 527-1, 2
Polyplastics Duranex® 531HS Polybutylene Terephthalate (PBT), Hydrolysis resistant, Heat shock resistant, Heat Shock Resistant DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Tensile Strength, Ultimate	118 MPa	17100 psi	ASTM D638
Toyobo Vylopet® EMC430 PET/PBT Blend Key Feature: HB UL-94 ClassApplications: general and high rigidity componentsPET/PBT blends suggested for glossy surfaces. General features of Vylopet® include heat resistance, good mechanical pro..
Tensile Strength, Ultimate	118 MPa	17100 psi	dry; ISO 527-1/-2
DSM Novamid® 1010GN2-15Z BK701 PA6-GF15 FR(17) 15% Glass Reinforced, Flame Retardant, Easy Molding Grade, Injection Molding, High Flow
Tensile Strength, Ultimate	118 MPa	17100 psi	cond; ISO 527-1/-2
DSM Novamid® 1015G33-8 NAT PA6-GF33 33% Glass Reinforced, Injection Molding
Tensile Strength, Ultimate	118 MPa	17100 psi	5mm/min; ISO 527
BASF Ultramid® 8231G HS BK-106 14% Glass Filled PA6 (Dry) Ultramid 8231G HS BK-106 is a black pigmented heat stabilized, 14% glass fiber reinforced PA6 injection molding compound.The glass fiber reinforcement enhances performance such as strength, stiffnes..
Tensile Strength, Ultimate	118 MPa	17100 psi	5mm/min; ISO 527
BASF Ultramid® 8267G HS BK-106A 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid 8267G HS BK-106A is a heat stabilized, weather resistant, 40% mineral and glass fiber reinforced PA6 injection molding compound with improved UV resistance and sink mark resistance. The co..
Tensile Strength, Ultimate	118 MPa	17100 psi	ASTM D638
A. Schulman ComAlloy Hiloy® 432 Glass Reinforced, PBT Alloy Data provided by the manufacturer, ComAlloy International Company.33% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate	118 MPa @Temperature 60.0 °C	17100 psi @Temperature 140 °F	ISO 527
LATI LARTON G/30 30% Glass Fiber Filled Polyphenylene sulfide (PPS) (discontinued **) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex..
Tensile Strength, Ultimate	118 MPa	17100 psi	DIN 53455; ASTM D638
Kolon KOPA® KN135G33HI Multi Reinforced Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubric..
Tensile Strength, Ultimate	118 MPa @Temperature 90.0 °C	17100 psi @Temperature 194 °F	ISO 527
LATI LARTON G/40 40% Glass Fiber Filled Polyphenylene sulfide (PPS) (Unverified Data**) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex..