BASF Ultramid® 1403-2 BK ND3007 PA66 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 1403-2 BK ND3007 PA66 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
dry; ISO 1183
Water Absorption 7.4 %
7.4 %
beginning dry; ISO 62
Moisture Absorption at Equilibrium 2.2 %
2.2 %
beginning dry (23°C/50% R.H.); ISO 62
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 90.0 MPa
13100 psi
5mm/min; ISO 527
Elongation at Break 13 %
13 %
5mm/min; ISO 527
Tensile Modulus 3.90 GPa
566 ksi
1mm/min; ISO 527
Flexural Modulus 3.00 GPa
435 ksi
ISO Data
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
ISO Test
Charpy Impact Unnotched 6.50 J/cm²
30.9 ft-lb/in²
ISO 179
4.50 J/cm²

@Temperature -30.0 °C
21.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
ISO 179
0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 257 °C
495 °F
10 K/min
257 °C
495 °F
ASTM Test
Descriptive Properties Value Comments
Color Black
Commercial Status Active America
Impact Modified No
Primary Processing Technique Injection Molding