BASF Luranyl® KR 2403 G4 Polyphenylene Ether + Styrene-Butadiene Blend, 20% Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether + Styrene-Butadiene Blend, Glass Filled , Styrene-Butadiene
Manufacturer	BASF
Trade Name	Luranyl®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Luranyl® KR 2403 G4 Polyphenylene Ether + Styrene-Butadiene Blend, 20% Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

General-purpose grade with 20% glass fiber for parts requiring especially good resistance to heat deformation.Applications: sanitary fittings and parts for fans, computer keyboards.Data was collected by ISO methods and provided by BASF.

Physical Properties	Metric	English
Density	1.20 g/cc	0.0434 lb/in³
Water Absorption	0.30 %	0.30 %
Moisture Absorption at Equilibrium	0.10 %	0.10 %
Linear Mold Shrinkage, Flow	0.0040 cm/cm	0.0040 in/in
High Load Melt Index	11 g/10 min @Load 21.6 kg, Temperature 250 °C	11 g/10 min @Load 47.6 lb, Temperature 482 °F

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	90.0 MPa	13100 psi
Elongation at Break	3.0 %	3.0 %
Tensile Modulus	6.50 GPa	943 ksi
Charpy Impact Unnotched	4.00 J/cm²	19.0 ft-lb/in²
	4.00 J/cm² @Temperature -30.0 °C	19.0 ft-lb/in² @Temperature -22.0 °F
Charpy Impact, Notched	1.30 J/cm²	6.19 ft-lb/in²
	1.30 J/cm² @Temperature -30.0 °C	6.19 ft-lb/in² @Temperature -22.0 °F
Tensile Creep Modulus, 1 hour	6100 MPa	885000 psi
Tensile Creep Modulus, 1000 hours	5150 MPa	747000 psi

Thermal Properties	Metric	English
CTE, linear, Parallel to Flow	45.0 µm/m-°C @Temperature 20.0 °C	25.0 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	142 °C	288 °F
Deflection Temperature at 1.8 MPa (264 psi)	139 °C	282 °F
Vicat Softening Point	142 °C	288 °F
Flammability, UL94	HB @Thickness 3.20 mm	HB @Thickness 0.126 in

Electrical Properties	Metric	English
Electrical Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Constant	2.9 @Frequency 100 Hz	2.9 @Frequency 100 Hz
	2.9 @Frequency 1e+6 Hz	2.9 @Frequency 1e+6 Hz
Dielectric Strength	95.0 kV/mm	2410 kV/in
Dissipation Factor	0.00080 @Frequency 1e+6 Hz	0.00080 @Frequency 1e+6 Hz
Comparative Tracking Index	250 V	250 V

Users viewing this material also viewed the following: