- SABIC Innovative Plastics LNP LUBRICOMP RL4040HSUV PA 66
SABIC Innovative Plastics LNP LUBRICOMP RL4040HSUV PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RL4040HSUV PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RL4040HSUV is a compound based on Nylon 66 containing 20% PTFE. Added features of this grade include: Heat Stabilized, UV Stabilized, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Density | 1.274 g/cc | 0.04603 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.750 % | 0.750 % | 50% RH, 24 hrs; ASTM D570 |
| 1.10 % | 1.10 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 5 mm/min; ISO 527 |
| 64.0 MPa | 9280 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 7.9 % | 7.9 % | Type I, 5 mm/min; ASTM D638 |
| 9.6 % | 9.6 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 5.1 % | 5.1 % | 5 mm/min; ISO 527 |
| 5.2 % | 5.2 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.79 GPa | 405 ksi | 1 mm/min; ISO 527 |
| 2.88 GPa | 418 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 97.0 MPa | 14100 psi | ISO 178 |
| Flexural Modulus | 2.55 GPa | 370 ksi | 2 mm/min; ISO 178 |
| 2.64 GPa | 383 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.83 J/cm | 12.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 42.0 kJ/m² | 20.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.22 | 0.22 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.11 | 0.11 | ASTM D3702 Modified |
| K (wear) Factor | 56.4 x 10-8 mm³/N-M | 28.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 112 µm/m-°C @Temperature -30.0 - 30.0 °C |
62.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 92.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
51.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 236 °C @Thickness 3.20 mm |
457 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3855 TPE, PP Overmold or Standalone use
- Polimeri Europa Riblene® MM 20 Low Density Polyethylene - Injection Molding
- Osprey Metals S2 Tool Steel Powder (Grade 95% - 16)
- Network Polymers SBN 150 Styrene Butadiene Acrylonitrile Terpolymer
- Paratherm Corporation Paratherm™ HT Heat Transfer Fluid
- LATI Latamid 66 H2 K/50 PA 66, 50% Carbon Fiber Reinforced, Heat Stabilized
- Techmer ES Plastiblend® PC/PET IM 1016 UV
- ChevronTexaco Molytex® EP NLGI Grade 2
- Cossa Polimeri ESTABLEND PA 1560 T8 GF ABS / Nylon 6 Blend, 30% Glass & Mineral Filled
- 3M Scotch-Weld™ 3748 Hot Melt Adhesive
Copyright © lookpolymers.com All Rights Reserved