Asahi Kasei Leona® 14G15 15% Glass Filled Nylon 66

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled
Manufacturer	Asahi Kasei
Trade Name	Leona®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Asahi Kasei Leona® 14G15 15% Glass Filled Nylon 66.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

15% Glass Fiber Reinforced. Enhanced strength and stiffnessApplications:Heater tanks, fuel injectors, ABS sensors, and other under-the-hood automotive parts Information provided by Asahi Kasei

Physical Properties	Metric	English	Comments
Specific Gravity	1.25 g/cc	1.25 g/cc	Dry; ASTM D792
Water Absorption	2.1 %	2.1 %	Wet
Linear Mold Shrinkage	0.0070 cm/cm	0.0070 in/in	Dry; ASTM D2863
Linear Mold Shrinkage, Transverse	0.012 cm/cm	0.012 in/in	Dry; ASTM D2863

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	71	71	Wet; ASTM D785
	94	94	Dry; ASTM D785
Hardness, Rockwell R	120	120	Dry; ASTM D785
Tensile Strength, Yield	79.0 MPa	11500 psi	Wet; ASTM D638
	108 MPa	15700 psi	Dry; ASTM D638
Elongation at Break	2.5 %	2.5 %	Dry; ASTM D638
	8.0 %	8.0 %	Wet; ASTM D638
Flexural Strength	108 MPa	15700 psi	Wet; ASTM D790
	167 MPa	24200 psi	Dry; ASTM D790
Flexural Modulus	2.50 GPa	363 ksi	Wet; ASTM D790
	4.90 GPa	711 ksi	Dry; ASTM D790
Izod Impact, Notched	0.490 J/cm	0.918 ft-lb/in	Dry; ASTM D256
	0.590 J/cm	1.11 ft-lb/in	Wet; ASTM D256
Taber Abrasion, mg/1000 Cycles	9.0	9.0	Wet; ASTM D1044

Thermal Properties	Metric	English	Comments
CTE, linear	40.0 µm/m-°C @Temperature 20.0 °C	22.2 µin/in-°F @Temperature 68.0 °F	Dry; ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	258 °C	496 °F	Dry; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	240 °C	464 °F	Dry; ASTM D648
Flammability, UL94	HB	HB	Dry