Polymer Property : Tensile Strength, Yield = 15700 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	108 - 200 MPa	15700 - 29000 psi	Average value: 133 MPa Grade Count:4
Overview of materials for Nylon 612, Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Carbon Fiber Filler". Each property range of values reported is minimum and maximum values of..
Tensile Strength, Yield	108 MPa	15700 psi	ASTM D638
LG Chemical LUPOY GP-5300 General Purpose PC/ABS Alloy, 30% Polymer Alloy, High Strength, Dimensional Stability Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive..
Tensile Strength, Yield	108 MPa	15700 psi	ASTM D638
Techmer ES HiFill FRÂ® PBT GF30 FR-S AS 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: AntistaticFeatures: Flame Retardant, Antistatic and Non-BloomingProcessing Method: Injection..
Tensile Strength, Yield	108 MPa	15700 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics ValoxÂ® CS860 PBT+PET (Asia Pacific) 30% glass reinforced PBT+PET blend. Color stable, FR. Housewares, appliances; iron skirt, oven trim/panels.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength, Yield	108 MPa	15700 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® ENH4560 PBT (Asia Pacific) Valox* ENH4560 resin is a non-brominated/non-chlorinated flame retardant product based on Valox* iQ PBT resin.
Tensile Strength, Yield	108 MPa	15700 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® IQ4860HR PBT Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified.
Tensile Strength, Yield	108 MPa	15700 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® IQ4860HR PBT (Asia Pacific) Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified.
Tensile Strength, Yield	108 MPa	15700 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® IQ4860HR PBT (Europe-Africa-Middle East) Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified.
Tensile Strength, Yield	108 MPa	15700 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® IQNH4560 PBT (Asia Pacific) Valox* IQNH4560 resin is a non-brominated/non-chlorinated flame retardant product based on Valox* iQ PBT resin.
Tensile Strength, Yield	108 MPa	15700 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP 9X02540 PC+PET LNP* THERMOCOMP* PDX-02540 is a compound based on a PET+PC Blend containing Proprietary Filler. Flame Retardant.
Tensile Strength, Yield	108 MPa	15700 psi	ASTM D638
Techmer ES LuriblendÂ® PC CF10 TL15 FR BK 10% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 10% Filler by WeightAdditive: PTFE LubricantFeatures: Lubricated and Flame RetardantAppearance: BlackInformation provided..
Tensile Strength, Yield	108 MPa	15700 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL IGN320 PPE+PS 20% glass reinforced PPE + PS. High heat, high modulus automotive applications like ignition coils.
Tensile Strength, Yield	108 MPa	15700 psi	SABIC - Japan Method
SABIC Innovative Plastics NORYL NF1030 PPE+PS (Asia Pacific)
Tensile Strength, Yield	108 MPa	15700 psi	At 50 mm/min; ISO 527-2
Borealis Xmod™ GD301HP High Performance 32% Glass Fiber Reinforced Xmod GD301HP is reinforced with 32% chemically coupled glass fibers and based on specific Polymer matrix material which is bringing excellent mechanical properties (impact behavior) and very good st..
Tensile Strength, Yield	108 MPa	15700 psi	chs 2.0 in/min; ASTM D638
Diamond Polymers DIAMALOY 1001 CF20 20% Carbon Fiber Filled ABS Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Tensile Strength, Yield	108 MPa	15700 psi	ASTM D638
Asahi Kasei Thermylene® P-40FG-0860 40% Glass Fiber Reinforced Information provided by Asahi Thermofil
Tensile Strength, Yield	108 MPa	15700 psi	Dry; ASTM D638
Asahi Kasei Leona® 14G15 15% Glass Filled Nylon 66 15% Glass Fiber Reinforced. Enhanced strength and stiffnessApplications:Heater tanks, fuel injectors, ABS sensors, and other under-the-hood automotive parts Information provided by Asahi Kasei
Tensile Strength, Yield	108 MPa	15700 psi	SABIC - Japan Method
SABIC Innovative Plastics NORYL CN5246 PPE+PS (Asia Pacific)