Arkema Group Rilsan® Clear G380 Renew Polyamide

Category	Polymer , Thermoplastic , Nylon
Manufacturer	Arkema
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Rilsan® Clear G380 Renew Polyamide.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Rilsan® Clear G830 Rnew is a high performance transparent polyamide partially based on renewable resources. This grade has been specially designed for injection molding applications, ideally suited for optics as high end eyewear frames.Information provided by Arkema Group

Physical Properties	Metric	English	Comments
Density	1.01 g/cc	0.0365 lb/in³	ISO R 1183 D
Water Absorption	1.3 %	1.3 %	at equilibrium at 23°C and 50 % RH; ISO 62
	3.3 %	3.3 %	at equilibrium at 23°C in water; ISO 62

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	83	83	instantaneous, conditioned 15 day, 23°C - 50 % R.H.; ISO 868
	81 @Time 15.0 sec	81 @Time 0.00417 hour	conditioned 15 day, 23°C - 50 % R.H.; ISO 868
Tensile Strength at Break	60.0 MPa	8700 psi	conditioned 15 days, 23°C - 50 % R.H.; ISO 527
Tensile Strength, Yield	55.0 MPa	7980 psi	conditioned 15 days, 23°C - 50 % R.H.; ISO 527
Elongation at Break	>= 150 %	>= 150 %	conditioned 15 days, 23°C - 50 % R.H.; ISO 527
Elongation at Yield	7.0 %	7.0 %	conditioned 15 days, 23°C - 50 % R.H.; ISO 527
Tensile Modulus	1.69 GPa	245 ksi	conditioned 15 days, 23°C - 50 % R.H.; ISO 527
Flexural Modulus	1.53 GPa	222 ksi	conditioned 15 days, 23°C - 50 % R.H.; ISO 178
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179/1eU
Charpy Impact, Notched	100 J/cm² @Temperature -30.0 °C	476 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	110 J/cm² @Temperature 23.0 °C	524 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	110 °C	230 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	95.0 °C	203 °F	ISO 75
Glass Transition Temp, Tg	135 °C	275 °F	ISO 11357
Shrinkage, MD	0.10 % @Thickness 2.00 mm	0.10 % @Thickness 0.0787 in	after 24h, mould at 40°C
Shrinkage, TD	0.50 % @Thickness 2.00 mm	0.50 % @Thickness 0.0787 in	after 24h, mould at 40°C

Optical Properties	Metric	English	Comments
Transmission, Visible	90 %	90 %	clear; thickness not quantified

Component Elements Properties	Metric	English	Comments
Carbon, C	53 - 55 %	53 - 55 %	renewable; ASTM 6866

Processing Properties	Metric	English	Comments
Processing Temperature	240 - 300 °C	464 - 572 °F	Injection
	270 °C	518 °F	Injection, recommended
Mold Temperature	20.0 - 80.0 °C	68.0 - 176 °F
Drying Temperature	70.0 - 80.0 °C	158 - 176 °F
Dry Time	4.00 - 6.00 hour	4.00 - 6.00 hour

Descriptive Properties	Value	Comments
Transparency	91.5%	560 nm, 2 mm; ISO 13168-1,2