Arkema Group Pebax® 3533 SA 01 Polyether Block Amide (PEBA)

Category	Polymer , Thermoplastic , Polyether Block Amide (PEBA)
Manufacturer	Arkema
Trade Name	Pebax®
Port	Shanghai port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Arkema Group Pebax® 3533 SA 01 Polyether Block Amide (PEBA).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Polyether block amide PEBAX® 3533 SA 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This SA grade is specially designed to food uses.Information provided by Arkema Group

Physical Properties	Metric	English	Comments
Density	1.00 g/cc	0.0361 lb/in³	ISO 1183
Water Absorption	1.2 % <br>@Temperature 23.0 °C,<br> Time 86400 sec	1.2 % <br>@Temperature 73.4 °F,<br> Time 24.0 hour	ISO 62
Moisture Absorption at Equilibrium	0.40 % <br>@Temperature 20.0 °C	0.40 % <br>@Temperature 68.0 °F	50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.0050 cm/cm <br>@Thickness 4.00 mm,<br> Time 86400 sec	0.0050 in/in <br>@Thickness 0.157 in,<br> Time 24.0 hour
Linear Mold Shrinkage, Transverse	0.0080 cm/cm <br>@Thickness 4.00 mm,<br> Time 86400 sec	0.0080 in/in <br>@Thickness 0.157 in,<br> Time 24.0 hour

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	33	33	Instantaneous, Conditioned 15 days at 23°C - 50% RH; ISO 868
	25 <br>@Time 15.0 sec	25 <br>@Time 0.00417 hour	Conditioned 15 days at 23°C - 50% RH; ISO 868
Tensile Strength at Break	39.0 MPa	5660 psi	Conditioned 15 days at 23°C - 50% RH; ASTM D638
Elongation at Break	>= 600 %	>= 600 %	Conditioned 15 days at 23°C - 50% RH; ASTM D638
Flexural Modulus	0.0210 GPa	3.05 ksi	Conditioned 15 days at 23°C - 50% RH; ISO178
Charpy Impact Unnotched	NB <br>@Temperature 23.0 °C	NB <br>@Temperature 73.4 °F	ISO 179
	NB <br>@Temperature -30.0 °C	NB <br>@Temperature -22.0 °F	ISO 179
Charpy Impact, Notched	NB <br>@Temperature 23.0 °C	NB <br>@Temperature 73.4 °F	ISO 179
	NB <br>@Temperature -30.0 °C	NB <br>@Temperature -22.0 °F	ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	144 °C	291 °F	ISO 11357
Vicat Softening Point	77.0 °C <br>@Load 1.02 kg	171 °F <br>@Load 2.25 lb	ISO 306

Processing Properties	Metric	English	Comments
Processing Temperature	205 °C	401 °F	Recommended Extrusion Temperature
	190 - 220 °C	374 - 428 °F	Extrusion Range
Nozzle Temperature	210 °C	410 °F	Recommended
	180 - 240 °C	356 - 464 °F
Mold Temperature	10.0 - 30.0 °C	50.0 - 86.0 °F
Drying Temperature	55.0 - 65.0 °C	131 - 149 °F
Dry Time	4.00 - 8.00 hour	4.00 - 8.00 hour

Users viewing this material also viewed the following: