Arkema Group Orgalloy® RS 6020 Nylon 6 Alloy, 20% Glass Fiber (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer Arkema
Trade Name Orgalloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Orgalloy® RS 6020 Nylon 6 Alloy, 20% Glass Fiber (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
RS 60 series, rigid polyamide 6 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properties.RS 6020: 20% glass fiber. Balanced properties between impact resistance, stiffness, density,. For injection molding and for extrusion of profiles.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
Water Absorption 2.6 %
2.6 %
Moisture Absorption at Equilibrium 1.0 %
1.0 %
Humidity Absorption
Melt Flow 5.0 g/10 min

@Load 2.16 kg,
Temperature 235 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 455 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 110 MPa
16000 psi
5 mm/min
Elongation at Break 3.6 %
3.6 %
5 mm/min
Tensile Modulus 4.95 GPa
718 ksi
1 mm/min
Charpy Impact, Notched 1.05 J/cm²
5.00 ft-lb/in²
0.840 J/cm²

@Temperature -30.0 °C
4.00 ft-lb/in²

@Temperature -22.0 °F
Tensile Creep Modulus, 1 hour 3800 MPa
551000 psi
Tensile Creep Modulus, 1000 hours 2680 MPa
389000 psi
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10°C/min
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
Dielectric Constant 2.6

@Frequency 100 Hz
2.6

@Frequency 100 Hz
3.3

@Frequency 1e+6 Hz
3.3

@Frequency 1e+6 Hz
Dielectric Strength 35.0 kV/mm
889 kV/in
Dissipation Factor 0.024

@Frequency 1e+6 Hz
0.024

@Frequency 1e+6 Hz
0.063

@Frequency 100 Hz
0.063

@Frequency 100 Hz
Comparative Tracking Index 600 V
600 V