Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 4.95 GPa | 718 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® BFL2015 PC Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only |
|||
Tensile Modulus | 4.95 GPa | 718 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® BFL2015 PC (Asia Pacific) Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only |
|||
Tensile Modulus | 4.95 GPa | 718 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® BFL2015 PC (Europe-Africa-Middle East) Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only |
|||
Tensile Modulus | 4.95 GPa | 718 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® BFL2015HF PC (Asia Pacific) Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only. UL94 V0 1.5 mm for BLACK; V1 1.5 mm for OTHER Color. |
|||
Tensile Modulus | 4.95 GPa | 718 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP PFI12R PA 6 LNP* LUBRICOMP* PFI12R is a compound based on Nylon 6 resin containing 10% Glass Fiber, 2% Silicone. Added features of this material include: Wear Resistant, Mold Release. |
|||
Tensile Modulus | 4.95 GPa | 718 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP PFI12R PA 6 (Asia Pacific) LNP* Lubricomp* PFI12R is a compound based on Nylon 6 resin containing Glass Fiber, Silicone. Added features of this material include: Internally Lubricated, Mold Release. |
|||
Tensile Modulus | 4.95 GPa | 718 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® 1760 PBT+PC 11% Glass Reinforced PBT+PC alloy. Impact/chemical resistant. Excellent physical property retention in automotive exteriors. |
|||
Tensile Modulus | 4.95 GPa | 718 ksi | 1 mm/min |
Arkema Group Orgalloy® RS 6020 Nylon 6 Alloy, 20% Glass Fiber (Conditioned) RS 60 series, rigid polyamide 6 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properties... |
|||
Tensile Modulus | 4.95 GPa @Temperature 80.0 °C |
718 ksi @Temperature 176 °F |
ISO Data |
BASF Petra® 130 30% Glass Filled PET Petra 130 is a 30% glass fiber reinforced polyethylene terephthalate (PET) for injection molding applications. It exhibits a good combination of performance properties including high strength and s.. |