Aclo Accutech Polypropylene Homopolymer HP0336T10L1 Talc Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0336T10L1 Talc Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | MD; ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 99 | 99 | ASTM D785 |
| Tensile Strength at Break | 23.0 MPa | 3340 psi | ASTM D638 |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | ASTM D638 |
| Elongation at Break | 22 % | 22 % | ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | ASTM D638 |
| Tensile Modulus | 1.40 GPa | 203 ksi | ASTM D638 |
| Flexural Strength | 49.0 MPa | 7110 psi | ASTM D790 |
| Flexural Modulus | 2.099 GPa | 304.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.299 J/cm | 0.560 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Zytel® HTN 52G45HSL BK083 Polyphthalamide (PPA) (Unverified Data**)
- Kennametal Stellite Delcrome 316L Iron Alloy
- LG Chemical LI933 Co-Extrusion ASA
- Intercontinental Polymers CoPET 198 CoPET Polymer Type - Clear, Low Melt Polyester Pellets
- SABIC Innovative Plastics LNP THERMOCOMP DB008ERP PC
- SABIC Innovative Plastics LNP Thermocomp DF002L PC (Asia Pacific)
- Fainplast Compounds GK 72/R Flexible PVC, Flame Retardant Sheathing Lead Free
- DuPont Teijin Films Mylar® RL4 Polyester Packaging Film, 50 Gauge
- Arlon LW401B##-P1 0.040" (1.02 mm) Cured Self-Fusing Silicone Tape (Triangular, Unsupported)
- Fainplast Compounds PMP 57 Flexible PVC, Extrusion Modified with PU
Copyright © lookpolymers.com All Rights Reserved