A. Schulman ComAlloy Lubrilon® 602 Nylon 6/6, Molybdenum Disulfide Filled, Flow Enhanced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, MoS2 Filled
Manufacturer A. Schulman ComAlloy
Trade Name Lubrilon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman ComAlloy Lubrilon® 602 Nylon 6/6, Molybdenum Disulfide Filled, Flow Enhanced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulman product line.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
Linear Mold Shrinkage 0.0080 cm/cm
0.0080 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength, Ultimate 94.0 MPa
13600 psi
ASTM D638
Elongation at Break 10 %
10 %
ASTM D638
Flexural Strength 129 MPa
18700 psi
ASTM D790
Flexural Modulus 3.40 GPa
493 ksi
ASTM D790
Izod Impact, Notched 0.270 J/cm
0.506 ft-lb/in
ASTM D256
Izod Impact, Unnotched 13.34 J/cm
24.99 ft-lb/in
ASTM D256
K (wear) Factor 302 x 10-8 mm³/N-M
150 x 10-10 in³-min/ft-lb-hr
K=W/PVT where W=wear (inches^3); P=applied pressure (psi); V=velocity (fpm); T=time (hours).
Limiting Pressure Velocity 0.490 MPa-m/sec
14000 psi-ft/min
Thermal Properties Metric English Comments
Melting Point 255 - 275 °C
491 - 527 °F
Deflection Temperature at 0.46 MPa (66 psi) 199 °C
390 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 79.0 °C
174 °F
ASTM D648
Processing Properties Metric English Comments
Processing Temperature 290 °C
554 °F
Approximate middle barrel temperature.