Polymer Property : Flexural Strength = 129 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 129 MPa
18700 psi
ASTM D 790
SABIC Innovative Plastics LNP Lubricomp DFL329EF PC
LNP LUBRICOMP* DFL329EF is a compound based on Polycarbonate resin containing Flame Retardant, Glass Fiber, PTFE. Added features of this material include: Flame Retardant.This data was supplied by ..
Flexural Strength 129 MPa
18700 psi
ISO 178
SABIC Innovative Plastics LNP Lubricomp DFP22H PC
LNP* Lubricomp* DFP22H is a compound based on Polycarbonate containing Glass Fiber and PTFE. Characteristics of this grade are: Internally Lubricated and Healthcare.This data was supplied by SABIC..
Flexural Strength 129 MPa
18700 psi
2mm/min; ASTM D790
Kingfa JH720 G15 15% Glass Fiber Reinforced PC
Features:Excellent balance propertiesHigh mechanical propertiesHigh stiffnessGood size stabilityGood surfaceApplications:Imaging equipment shellOA body frameElectrical equipmentComputer plug partsIn..
Flexural Strength 129 MPa
18700 psi
ISO 178
Solvay TECHNYL® A 548B2 V15 PA66, 15% glass fiber, DRY
Description: TECHNYL® A 548B2 V15 is a polyamide 6.6, reinforced with 15% of glass fiber, heat stabilized, impact modified, for blow molding. This product is available in black color.Benefits: Th..
Flexural Strength 129 MPa
18700 psi
ASTM D 790
SABIC Innovative Plastics LNP Lubricomp UX06442 PPA
LNP* Lubricomp* UX06442 is a compound based on Polyphthalamide resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.This data was supplied by SABIC..
Flexural Strength 129 MPa
18700 psi
ASTM D 790
SABIC Innovative Plastics LNP Lubricomp UX06442 PPA (Asia Pacific)
LNP* Lubricomp* UX06442 is a compound based on Polyphthalamide resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.This data was supplied by SABIC..
Flexural Strength 129 MPa
18700 psi
ASTM D790
Techmer ES HiFill® PA12 CM40 40% Mineral Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Mineral Filler, 40% Filler by WeightAdditive: LubricantFeatures: LubricatedInformation provided by TP Composites, Inc.
Flexural Strength 129 MPa
18700 psi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DF0029ER PC (Asia Pacific)
LNP* Thermocomp* DF0029ER is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Flame Retardant.
Flexural Strength 129 MPa
18700 psi
ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP KF002 Acetal Copolymer
LNP THERMOCOMP* KF002 is a compound based on Acetal Copolymer resin containing 10% Glass Fiber.
Flexural Strength 129 MPa
18700 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermocomp MF008S PP (Europe-Africa-Middle East)
Heat Stabilized Polypropylene compound containing Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Strength 129 MPa
18700 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL PPX PPX630 PPE+PP
30% GR PPE+PP. High elongation. high stiffness. NSF Standard 61 Compliant (color limited).
Flexural Strength 129 MPa
18700 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL PPX PPX630 PPE+PP (Asia Pacific)
30% GR PPE+PP. High elongation. high stiffness. NSF Standard 61 Compliant (color limited).
Flexural Strength 129 MPa
18700 psi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DF0029ER PC
LNP* Thermocomp* DF0029ER is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Flame Retardant.
Flexural Strength 129 MPa
18700 psi
ISO 178
Polyplastics Duranex® 361SA Polybutylene Terephthalate (PBT), Low density, Low wear, GF filled
DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Flexural Strength 129 MPa
18700 psi
Outer Fiber Stress at 3.5% Outer Fiber Strain; DIN EN ISO 178
Wolf Kunststoff ZEDEX® ZX-410V7T A4T Polymer Alloy, Fiber Reinforced, Friction Modified
Main Characteristics: Fiber-reinforced; Friction-modified; Very high stiffness (higher than that of fiber-reinforced PEEK); Very low thermal expansion coefficient; Low friction; High wear resistance..
Flexural Strength 129 MPa
18700 psi
2 mm/min; ISO 178
Eurostar Starpylen MF008S PP, 40% Glass Fiber Filled, Injection Molded
Starpylen MF008S is a 40% Glass Fiber Reinforced Polypropylene Injection Molding ResinInformation provided by Eurostar.
Flexural Strength 129 MPa
18700 psi
ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0334G10M20CL Glass/Mineral Reinforced Coupled
Flexural Strength 129 MPa
18700 psi
ASTM D790
A. Schulman ComAlloy Lubrilon® 602 Nylon 6/6, Molybdenum Disulfide Filled, Flow Enhanced
Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
Flexural Strength 129 MPa
18700 psi
perpendicular
Carlisle 201LD Carbon-Carbon Composite
Carbon-Carbon Composite manufactured as sheets from 4mm to 125mm thick this material is essentially a fracture tough, fiber reinforced graphite often referred to as a “CFC”. Good for use in air t..
Flexural Strength 129 MPa
18700 psi
Mitsui AURUM® JCR3030F Thermoplastic Polyimide Resin, Wear/Friction Grade  (discontinued **)
AURUM® is an easy melt, processable and recyclable thermoplastic polyimide resin that provides continuous service temperatures to 465° F in its amorphous state and up to 550° F when annealed to i..
Flexural Strength 129 MPa
18700 psi
ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DFL329 PC
LNP LUBRICOMP* DFL329 is a compound based on Polycarbonate resin containing 10% Glass Fiber, 15% PTFE. Added features of this material include: Flame Retardant, Internally Lubricated.
Flexural Strength 129 MPa
18700 psi
ASTM D 790
SABIC Innovative Plastics Valox® VSR4150 PBT (Asia Pacific)
This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Strength 129 - 157 MPa
18700 - 22700 psi
Bulk Molding Compounds BMC T40(20) Die Casting Replacement Grade Molding Compound
BMC T40(20) was formulated as a direct replacement for aluminum die casting applications. T40(20) is UL recognized. Excellent mechanical properties and dimensional control allow molded parts to ma..