Polymer Property : Tensile Strength, Ultimate = 94.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 94.0 - 179.953 MPa

@Temperature -40.0 - 120 °C
13600 - 26100.0 psi

@Temperature -40.0 - 248 °F
Average value: 142 MPa Grade Count:3
Overview of materials for Polyphenylene Sulfide (PPS) with 50% Glass Fiber Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 50% Glass Fiber Filler". Specific grades with glass content between 45%..
Tensile Strength, Ultimate 94.0 MPa
13600 psi
ISO 527-1, 2
Polyplastics Duranex® CRN7830 Polybutylene Terephthalate (PBT), Lower noise, 30% GF filled
DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Tensile Strength, Ultimate 94.0 MPa
13600 psi
ISO 527-1, 2
Polyplastics Duranex® 7400W Polybutylene Terephthalate (PBT), Super low warpage, GF filled
DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Tensile Strength, Ultimate 94.0 MPa
13600 psi
ATSM D638
Ashley Polymers Ashlene® 527LD-13G Nylon 66, 13% Glass Reinforced
A high impact 13% glass reinforced Nylon 66.Data provided by the manufacturer
Tensile Strength, Ultimate 94.0 MPa
13600 psi
ATSM D638
Ashley Polymers Ashlene® 527LD-14G Nylon 66, 14% Glass Reinforced
A high impact nylon with 14% glass.Data provided by the manufacturer
Tensile Strength, Ultimate 94.0 MPa
13600 psi
ASTM D638
Chem Polymer Chemlon 100 W Nylon 66, MoS2 Filled
A molybdenum disulfide modified nylon 66 exhibiting superior tensile strength and wear resistance, greater dimensional stability and higher heat resistance than general purpose nylon 66.Data provide..
Tensile Strength, Ultimate 94.0 MPa
13600 psi
ASTM D638
A. Schulman ComAlloy Lubrilon® 602 Nylon 6/6, Molybdenum Disulfide Filled, Flow Enhanced
Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
Tensile Strength, Ultimate 94.0 MPa
13600 psi
ASTM D638
A. Schulman ComAlloy Voloy® 415 Polyester - PBT, Glass/Mineral Reinforced, Flame Retardant, UL
Data provided by the manufacturer, ComAlloy International Company.30% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate 94.0 MPa
13600 psi
ASTM D638
A. Schulman ComAlloy Voloy® 612 Nylon 6, Glass Fiber/Bead Reinforced, Flame Retardant, UL
Data provided by the manufacturer, ComAlloy International Company.30% Glass Fiber/Bead Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate 94.0 MPa

@Temperature 120 °C
13600 psi

@Temperature 248 °F
ISO 527
LATI LARTON G/50 50% Glass Fiber Filled Polyphenylene sulfide (PPS)  (discontinued **)
Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex..