Kingfa PA66-RG301 Flame Retardant, 30% Glass Fiber Reinforced PA66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant
Manufacturer Kingfa Sci. & Tech. Co.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kingfa PA66-RG301 Flame Retardant, 30% Glass Fiber Reinforced PA66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features:Flame retardantHigh strengthHigh temperature propertiesGood electric propertiesNo bloomingApplications:Injection moldingConnectorsRelayBobbinsPlugsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.46 g/cc

@Temperature 23.0 °C
1.46 g/cc

@Temperature 73.4 °F
ASTM D792
Water Absorption 0.60 %

@Temperature 23.0 °C,
Time 86400 sec
0.60 %

@Temperature 73.4 °F,
Time 24.0 hour
ASTM D570
Linear Mold Shrinkage 0.0040 - 0.0090 cm/cm

@Temperature 23.0 °C
0.0040 - 0.0090 in/in

@Temperature 73.4 °F
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength at Break 155 MPa
22500 psi
10mm/min; ASTM D638
Elongation at Break 2.1 %
2.1 %
10mm/min; ASTM D638
Flexural Strength 220 MPa
31900 psi
2mm/min; ASTM D790
Flexural Modulus 8.80 GPa
1280 ksi
2mm/min; ASTM D790
Izod Impact, Notched 0.950 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
1.78 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 257 °C

@Thickness 6.40 mm
495 °F

@Thickness 0.252 in
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 250 °C

@Thickness 6.40 mm
482 °F

@Thickness 0.252 in
ASTM D648
Flammability, UL94 V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Processing Temperature <= 310 °C
<= 590 °F
Rear Barrel Temperature 255 - 275 °C
491 - 527 °F
Start Point: 265°C
Middle Barrel Temperature 260 - 290 °C
500 - 554 °F
Start Point: 280°C
Front Barrel Temperature 270 - 300 °C
518 - 572 °F
Start Point: 285°C
Melt Temperature 275 - 300 °C
527 - 572 °F
Start Point: 285°C
Mold Temperature 50.0 - 70.0 °C
122 - 158 °F
Start Point: 60°C
Drying Temperature 90.0 - 110 °C

@Time 14400 - 21600 sec
194 - 230 °F

@Time 4.00 - 6.00 hour
Pre-dry
Descriptive Properties Value Comments
Glass Fiber Content (%) 30
Injection Speed Moderate to High