- Lubrizol Pellethane® 2363-75D Thermoplastic Polyurethane Elastomer
Lubrizol Pellethane® 2363-75D Thermoplastic Polyurethane Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | Pellethane® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Pellethane® 2363-75D Thermoplastic Polyurethane Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0080 cm/cm | 0.0030 - 0.0080 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 28 g/10 min @Load 5.00 kg, Temperature 224 °C |
28 g/10 min @Load 11.0 lb, Temperature 435 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 76 | 76 | ASTM D2240 |
| Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM D412 |
| Elongation at Break | 380 % | 380 % | ASTM D412 |
| Flexural Modulus | 1.30 GPa | 189 ksi | ASTM D790 |
| Tear Strength | 257 kN/m | 1470 pli | Die C; ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 55 | 55 | H22 Wheel, 1000g; ASTM D1044 |
| Tensile Set | 50 % | 50 % | Elongation Set After Break; ASTM D412 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 88.7 µm/m-°C @Temperature -80.0 - -30.0 °C |
49.3 µin/in-°F @Temperature -112 - -22.0 °F |
ASTM D696 |
| Vicat Softening Point | 116 °C | 241 °F | 120°C/hr, 9.8N; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 204 - 221 °C | 399 - 430 °F | Extrusion |
| 210 - 227 °C | 410 - 441 °F | Molding | |
| Mold Temperature | 16.0 - 60.0 °C | 60.8 - 140 °F | |
| Drying Temperature | 99.0 - 110 °C | 210 - 230 °F | air dew point <-40°C |
Users viewing this material also viewed the following:
- Polykemi AB SCANAMID 66 A11^ X30 LS Nylon 66, Glass Reinforced, Laser Printable
- Zircar Zirconia CeW-30 Ceria Woven Textile Insulation
- Magnesium Elektron Elektron® 675 Magnesium Wrought Alloy
- DuPont™ Surlyn® 9150 Ionomer Resin, Zinc
- Aclo Accutech Polypropylene Homopolymer HP0339C20L1 Calcium Reinforced
- 3M 2262T Adhesion Promoter
Copyright © lookpolymers.com All Rights Reserved