- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 126 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 126 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | |
| Plastcom SLOVALEN PC 63 T 15-1M PP, 15% mineral filling FeaturesModified PP copolymer for injection moulding with the content of 15 % mineral filler, uv stabilized, good scratch resistance, low odor and very good flowability with good dimensional stabili.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F | ASTM D648 |
| RheTech Products P252-670UV Polypropylene Copolymer, UV Stabilized, 134B Stone Applications: Interior trimElectrical housingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYblend 6005 PC/ABS-Blend Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYblend 6005B PC/ABS-Blend Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | Conditioned 4 hours @ 70°C (158°F); ASTM D648 |
| Eastman Tenite Butyrate 513E3720008 Clear, Trsp Cellulose Acetate Butyrate
(discontinued **) Plasticizer 23%. Weight loss on heating = 1.2% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 2-9000 Polypropylene Block-Copolymer INNOPOL® CS 2-9000 is a polypropylene block-copolymer based compound. This grade is available in nature and custom colored form.INNOPOL® CS 2-9000 is developed for producing injection molded a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F | Unannealed; ISO 75A-1, -2 |
| LyondellBasell Hostacomâ„¢ CA278A Thermoplastic Polyolefin Elastomer Description: Hostacomâ„¢ CA278A is a thermoplastic polyolefin elastomer that is used for automotive interior partsFeatures: Good StiffnessHigh FlowGood MoldabilityGood Impact ResistanceLow Temper.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C @Thickness 3.20 mm |
126 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON MD000IS PP LNP STAT-KON* MD000IS is a compound based on Polypropylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON MX01767C PP LNP* STAT-KON* MX01767C is a compound based on Polypropylene containing Proprietary Filler(s). Added features of this grade include: Electrically Conductive, Clean Compounding System. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON MX10301C PP LNP* STAT-KON* MX10301C is a compound based on Polypropylene containing Proprietary Filler(s). Added features of this grade include: Electrically Conductive, Clean Compounding System. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C @Thickness 3.20 mm |
126 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP 2Z004 ETFE LNP* THERMOCOMP* 2Z004 is a compound based on ETFE resin containing 20% Milled Glass. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | Unannealed; ISO 75-2/Af |
| Styron DGF080.00 ESU Polypropylene Overview: 10% glass filled polypropyleneNaturalMedium flowHeat ResistantInformation provided by Styron |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ISO 75 B |
| Borealis Borsoft™ SF203CF Soft Polypropylene Copolymer for Extrusion Coating Borsoft SF203CF is a new statistic-heterophasic propylene-ethylene copolymer suitable for coating applications. Its polymer structure permits perfect adhesion to certain products. According to the.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ISO 75-2 |
| Borealis Daplen™ HJ060UB Polypropylene Compound for Direct Left Manufactured Applications Daplen FJ060UB is a special low viscosity compound for direct LFT manufacturing process. It interacts perfectly with glass fibers to create excellent stiffness and impact resistance. Daplen HJ060U.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ISO 75-2 |
| Borealis HB601WG Polypropylene Homopolymer HB601WG is a polypropylene homopolymer intended for injection molding and blow molding. The product is available in natural but other colors can be provided on request. This material has excellent .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 1498HU UV Stabilized, Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1498HU is a high flow UV stabilized medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | 120°C per hour; ISO 752 |
| Total PPM H250 Polypropylene, Homopolymer Medical Grade Polypropylene PPM H250 is a narrow molecular weight distribution homopolymer with a Melt Flow Index of 25 g/10 min recommended for the manufacture of medical packaging and medical devices, to the ex.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ISO 75-2 |
| Borealis Daplen™ EF261AI Polypropylene TPO Compound Daplen™ EF261AI is a 20 % mineral filled polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and is easy to process... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ASTM D648 |
| Formosa Plastics Formolene® 6535N Impact Copolymer Polypropylene Impact Copolymer - Designed to Meet the Physical Requirements of Automotive Interior Trim Formolene® 6535N is an engineered, medium impact copolymer polypropylene. It was specifically developed to.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | Conditioned 4 hours @ 70°C (158°F); ASTM D648 |
| Eastman Tenite Butyrate 565A3720023 Clear, Trsp Cellulose Acetate Butyrate Plasticizer 23%. Weight loss on heating = 1.2% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F | ISO 75-2/A |
| ExxonMobil PP1063L1 Polypropylene Homopolymer Product Description: A homopolymer resin designed for general use. It is suitable for masterbatch carrier and other compounding applications and for the molding of caps, cups, containers and other .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | DAM; ASTM D648 |
| DuPont Performance Polymers Zytel® ST811HS NC010 Nylon 6
(Unverified Data**) Zytel® ST811HS is a flexible, heat stabilized Super Tough polyamide 6 resin developed for extrusion and injection molding applications such as cable and rope jacketing, hose inner cores and fastene.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | |
| Arkema Group Rilsan® BECN W3 TL Nylon 11, Sheathing Grade (Conditioned) Designation ISO 1874-PA11,KFHL,12-010Rigid grade for sheathing wires and cables. Available color: natural. Light and heat stabilized. Flame retardant agent.Fire-resistant. High abrasion resistance. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ASTM D648 |
| Ashley Polymers Ashlene® D930H Nylon 12 A plasticized Nylon 12 offering improved flexibility with superior moisture and chemical resistance. Also UV and heat stabilized, available in natural and precolored. Any color other than natural .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ASTM D648 |
| Ashley Polymers Ashlene® L930 Nylon 12 A plasticized Nylon 12 offering improved flexibility with superior moisture and chemical resistance. The natural color is slightly darker.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F | |
| Aclo Accutech Polypropylene Copolymer CP0436T10L Talc Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ASTM D648 |
| Braskem H 401 Cast Film Extrusion Polypropylene Description: H 401 is a medium melt flow rate homopolymer polypropylene, additived with slip and antiblocking agents. Designed specially for cast film. This product features good impact strength, ex.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 - 101 °C | 126 - 214 °F | Average value: 67.8 °C Grade Count:4 |
| Overview of materials for Polypropylene, Sheet/Thermoforming Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Sheet/Thermoforming Grade". Each property range of values reported is minimum and maximum.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C @Thickness 3.20 mm |
126 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON MS000IL PP LNP* STAT-KON* MS000IL is a compound based on Polypropylene resin containing Stainless Steel. Added features of this material include: High Impact, Low Extractible, Electrically Conductive, food c.. |
|||