Polykemi AB POLYblend 6005 PC/ABS-Blend

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer	Polykemi AB
Trade Name	POLYblend
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polykemi AB POLYblend 6005 PC/ABS-Blend.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Information provided by Polykemi AB

Physical Properties	Metric	English	Comments
Density	1.08 g/cc	0.0390 lb/in³	ISO 1183
Linear Mold Shrinkage	0.0080 - 0.010 cm/cm	0.0080 - 0.010 in/in	With Flow; ISO 2577
	0.0080 - 0.010 cm/cm	0.0080 - 0.010 in/in	Across Flow; ISO 2577
Melt Index of Compound	14 g/10 min @Load 5.00 kg, Temperature 240 °C	14 g/10 min @Load 11.0 lb, Temperature 464 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	62 @Time 15.0 sec	62 @Time 0.00417 hour	ASTM D2240
Tensile Strength at Break	<= 45.0 MPa	<= 6530 psi	ISO/R527
Elongation at Break	>= 80 %	>= 80 %	ISO/R527
Flexural Strength	<= 60.0 MPa	<= 8700 psi	ISO 178
Flexural Modulus	1.80 GPa @Temperature 23.0 °C	261 ksi @Temperature 73.4 °F	ISO 178
Charpy Impact, Notched	5.00 J/cm² @Temperature 23.0 °C	23.8 ft-lb/in² @Temperature 73.4 °F	ISO 179

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	96.0 °C	205 °F	120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi)	52.0 °C	126 °F	120°C/h; ISO 75/1
Vicat Softening Point	110 °C @Load 5.001 kg	230 °F @Load 11.03 lb	50°C/h; ISO 306
	190 °C @Load 1.00 kg	374 °F @Load 2.21 lb	50°C/h; ISO 306
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
Glow Wire Test	650 °C @Thickness 2.00 mm	1200 °F @Thickness 0.0787 in	IEC 695-2-1