Overview of materials for Polypropylene, Sheet/Thermoforming Grade

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Sheet/Thermoforming Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polypropylene, Sheet/Thermoforming Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Sheet/Thermoforming Grade". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.900 - 1.13 g/cc
0.0325 - 0.0408 lb/in³
Average value: 0.919 g/cc Grade Count:40
Oxygen Transmission 95.0 cc-mm/m²-24hr-atm
241 cc-mil/100 in²-24hr-atm
Average value: 95.0 cc-mm/m²-24hr-atm Grade Count:3
Thickness 25.4 - 1000 microns
1.00 - 39.4 mil
Average value: 553 microns Grade Count:9
Melt Flow 0.450 - 8.00 g/10 min
0.450 - 8.00 g/10 min
Average value: 2.26 g/10 min Grade Count:38
Surface Tension 48.0 dynes/cm
48.0 dynes/cm
Average value: 48.0 dynes/cm Grade Count:6
Mechanical Properties Metric English Comments
Hardness, Rockwell R 84.0 - 110
84.0 - 110
Average value: 96.1 Grade Count:16
Tensile Strength, Ultimate 30.0 - 35.9 MPa
4350 - 5210 psi
Average value: 33.9 MPa Grade Count:3
Film Tensile Strength at Yield, MD 20.0 - 37.0 MPa
2900 - 5370 psi
Average value: 28.0 MPa Grade Count:10
Film Tensile Strength at Yield, TD 16.0 - 36.0 MPa
2320 - 5220 psi
Average value: 25.3 MPa Grade Count:10
Tensile Strength, Yield 19.3 - 45.0 MPa
2800 - 6530 psi
Average value: 34.2 MPa Grade Count:35
Film Elongation at Break, MD 50.0 - 700 %
50.0 - 700 %
Average value: 453 % Grade Count:9
Film Elongation at Break, TD 6.00 - 850 %
6.00 - 850 %
Average value: 319 % Grade Count:9
Film Elongation at Yield, MD 14.0 - 24.0 %
14.0 - 24.0 %
Average value: 18.9 % Grade Count:9
Film Elongation at Yield, TD 9.00 - 23.0 %
9.00 - 23.0 %
Average value: 15.4 % Grade Count:9
Elongation at Break 9.00 - 11.0 %
9.00 - 11.0 %
Average value: 10.0 % Grade Count:4
Elongation at Yield 4.00 - 65.0 %
4.00 - 65.0 %
Average value: 11.5 % Grade Count:29
Modulus of Elasticity 0.280 - 2.05 GPa
40.6 - 297 ksi
Average value: 0.710 GPa Grade Count:12
Flexural Modulus 0.896 - 2.30 GPa
130 - 334 ksi
Average value: 1.52 GPa Grade Count:39
Izod Impact, Notched 0.210 - 981 J/cm
0.393 - 1840 ft-lb/in
Average value: 1.83 J/cm Grade Count:39
0.214 - 2.98984 J/cm

@Temperature -20.0 - 4.00 °C
0.401 - 5.60120 ft-lb/in

@Temperature -4.00 - 39.2 °F
Average value: 1.14 J/cm Grade Count:7
0.500 - 3.00 J/cm

@Temperature -20.0 - 0.000 °C
0.937 - 5.62 ft-lb/in

@Temperature -4.00 - 32.0 °F
Average value: 1.14 J/cm Grade Count:4
0.500 - 3.00 J/cm

@Thickness 3.20 - 3.20 mm
0.937 - 5.62 ft-lb/in

@Thickness 0.126 - 0.126 in
Average value: 1.14 J/cm Grade Count:4
Dart Drop, Total Energy 5.50 - 21.0 J
4.06 - 15.5 ft-lb
Average value: 9.50 J Grade Count:4
2.00 - 30.7 J

@Temperature -20.0 - 0.000 °C
1.48 - 22.6 ft-lb

@Temperature -4.00 - 32.0 °F
Average value: 12.7 J Grade Count:2
Tear Strength 130 - 230 kN/m
742 - 1310 pli
Average value: 180 kN/m Grade Count:4
Dart Drop Total Energy 55.0 - 60.0 J/cm
0.103 - 0.112 ft-lb/mil
Average value: 56.7 J/cm Grade Count:3
20.0 - 55.0 J/cm

@Temperature -20.0 - 0.000 °C
0.0375 - 0.103 ft-lb/mil

@Temperature -4.00 - 32.0 °F
Average value: 37.5 J/cm Grade Count:1
Thermal Properties Metric English Comments
Melting Point 147 - 165 °C
297 - 329 °F
Average value: 160 °C Grade Count:11
Deflection Temperature at 0.46 MPa (66 psi) 76.1 - 130 °C
169 - 266 °F
Average value: 107 °C Grade Count:36
Deflection Temperature at 1.8 MPa (264 psi) 52.0 - 101 °C
126 - 214 °F
Average value: 67.8 °C Grade Count:4
Vicat Softening Point 78.0 - 159 °C
172 - 318 °F
Average value: 141 °C Grade Count:18
Heat Distortion Temperature 79.0 - 110 °C
174 - 230 °F
Average value: 88.1 °C Grade Count:8
Optical Properties Metric English Comments
Haze 2.60 - 46.0 %
2.60 - 46.0 %
Average value: 19.8 % Grade Count:13
Gloss 80.0 - 110 %
80.0 - 110 %
Average value: 93.7 % Grade Count:3
Transmission, Visible 90.0 - 99.5 %
90.0 - 99.5 %
Average value: 94.4 % Grade Count:4
Processing Properties Metric English Comments
Melt Temperature 199 - 260 °C
390 - 500 °F
Average value: 235 °C Grade Count:4