Inno-Comp INNOPOLÂ® CS 2-9000 Polypropylene Block-Copolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer	Inno-Comp Ltd
Trade Name	INNOPOL® CS
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Inno-Comp INNOPOLÂ® CS 2-9000 Polypropylene Block-Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

INNOPOLÂ® CS 2-9000 is a polypropylene block-copolymer based compound. This grade is available in nature and custom colored form.INNOPOLÂ® CS 2-9000 is developed for producing injection molded automotive components.All information provided by INNO-COMP.

Physical Properties	Metric	English	Comments
Density	0.900 g/cc @Temperature 23.0 Â°C	0.0325 lb/inÂ³ @Temperature 73.4 Â°F	ISO 1183
Linear Mold Shrinkage	0.011 cm/cm	0.011 in/in	Normal; ISO 294
Linear Mold Shrinkage, Flow	0.013 cm/cm	0.013 in/in	ISO 294
Melt Flow	40 g/10 min @Load 2.16 kg, Temperature 230 Â°C	40 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	26.0 MPa	3770 psi	50 mm/min; ISO 527-1,-2
Elongation at Yield	8.0 %	8.0 %	50 mm/min; ISO 527-1,-2
Tensile Modulus	1.20 GPa	174 ksi	1 mm/min; ISO 527-1,-2
Charpy Impact, Notched	0.400 J/cmÂ² @Temperature -30.0 Â°C	1.90 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179/1eA
	0.800 J/cmÂ² @Temperature 23.0 Â°C	3.81 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	105 Â°C	221 Â°F	ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi)	52.0 Â°C	126 Â°F	ISO 75-1,-2
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in	FMVSS 302

Descriptive Properties	Value	Comments
Automotive Materials	Pass	FMVSS 302
Color	Natural