Borealis HB601WG Polypropylene Homopolymer

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Borealis
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis HB601WG Polypropylene Homopolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
HB601WG is a polypropylene homopolymer intended for injection molding and blow molding. The product is available in natural but other colors can be provided on request. This material has excellent balanced mechanical properties and is easy to process. Applications: HB601WG has been developed especially for applications like household applications, dishwasher components, and washing machine parts.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.900 g/cc
0.0325 lb/in³
ISO 1183
Linear Mold Shrinkage 0.013 cm/cm
0.013 in/in
average process; cross flow; 150x80x2mm
0.014 cm/cm
0.014 in/in
average process; in flow; 150x80x2mm
Melt Flow 2.2 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.2 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 65.0 MPa
9430 psi
358 N/30s; ISO 2039
Tensile Strength, Yield 34.0 MPa
4930 psi
ISO 527-2
Elongation at Yield 10 %
10 %
50mm/min; ISO 527-2
Tensile Modulus 1.40 GPa
203 ksi
1mm/min; ISO 527-2
Flexural Strength 40.0 MPa
5800 psi
ISO 178
Flexural Modulus 1.40 GPa
203 ksi
5mm/min; ISO 178
Charpy Impact Unnotched 2.00 J/cm²

@Temperature -20.0 °C
9.52 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 85.0 °C
185 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 52.0 °C
126 °F
ISO 75-2
Vicat Softening Point 90.0 °C

@Load 5.10 kg
194 °F

@Load 11.2 lb
ISO 306
154 °C

@Load 1.02 kg
309 °F

@Load 2.25 lb
ISO 306
Processing Properties Metric English Comments
Processing Temperature 220 - 260 °C
428 - 500 °F
mass temperature
Feed Temperature 40.0 - 80.0 °C
104 - 176 °F
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F
Injection Velocity 100 - 200 mm/sec
3.94 - 7.87 in/sec
Hold Pressure 30.0 - 60.0 MPa
4350 - 8700 psi
Descriptive Properties Value Comments
Back Pressure low to medium
Screw Speed low to medium