3M Scotch-Weld™ DP460 Off-White Epoxy Adhesive

Category Polymer , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer 3M
Trade Name Scotch-Weld™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Scotch-Weld™ DP460 Off-White Epoxy Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Scotch-Weld™ Epoxy Adhesive DP460 Off-White and DP460 NS are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion and very high levels of durability.Information provided by 3M
Physical Properties Metric English Comments
Viscosity 8000 - 14000 cP
8000 - 14000 cP
Accelerator
20000 - 50000 cP
20000 - 50000 cP
Base
Mechanical Properties Metric English Comments
Hardness, Shore D 75 - 80
75 - 80
Shear Strength 0.689 MPa
100 psi
Overlap, Isopropyl Alcohol Wipe surface prep, Neoprene/Steel
0.827 MPa
120 psi
Overlap, Isopropyl Alcohol/Abrade/Isopropyl Alcohol surface prep, Neoprene/Steel
0.965 MPa
140 psi
Overlap, Isopropyl Alcohol/Abrade/Isopropyl Alcohol surface prep, SBR/Steel
1.03 MPa
150 psi
Overlap, Isopropyl Alcohol Wipe surface prep, SBR/Steel
1.52 MPa
220 psi
Overlap, Isopropyl Alcohol Wipe surface prep, Polyacrylic
2.07 MPa
300 psi
Overlap, Isopropyl Alcohol Wipe surface prep, ABS
2.28 MPa
330 psi
Overlap, Isopropyl Alcohol/Abrade/Isopropyl Alcohol surface prep, Polyacrylic
2.41 MPa
350 psi
Overlap, Isopropyl Alcohol/Abrade/Isopropyl Alcohol surface prep, PVC
2.76 MPa
400 psi
Overlap, Isopropyl Alcohol Wipe surface prep, Polycarbonate
3.10 MPa
450 psi
Overlap, Isopropyl Alcohol Wipe surface prep, Polystyrene
3.28 MPa
475 psi
Overlap, Isopropyl Alcohol/Abrade/Isopropyl Alcohol surface prep, Polystyrene
3.45 MPa
500 psi
Overlap, Isopropyl Alcohol Wipe surface prep, PVC
3.45 MPa
500 psi
Overlap, Isopropyl Alcohol/Abrade/Isopropyl Alcohol surface prep, Polycarbonate
3.96 MPa
575 psi
Overlap, Isopropyl Alcohol/Abrade/Isopropyl Alcohol surface prep, ABS
5.52 MPa
800 psi
Overlap, Isopropyl Alcohol Wipe surface prep, FRP
6.89 MPa
1000 psi
Overlap, Isopropyl Alcohol/Abrade/Isopropyl Alcohol Wipe surface prep, FRP
9.65 MPa
1400 psi
Overlap, Isopropyl Alcohol Wipe surface prep, Phenolic
9.65 MPa
1400 psi
Overlap, Isopropyl Alcohol/Abrade/Isopropyl Alcohol surface prep, Phenolic
13.8 MPa
2000 psi
Overlap, Galvanized Steel Okite degrease Hot dip
14.5 MPa
2100 psi
Overlap, Galvanized Steel Okite degrease Electrodeposited
19.3 MPa
2800 psi
Overlap, CRS MEK/abrade/MEK
22.1 MPa
3200 psi
Overlap, Aluminum Oakite degrease
24.1 MPa
3500 psi
Overlap, Aluminum MEK/abrade/MEK
24.1 MPa
3500 psi
Overlap, CRS Oakite degrease
27.6 MPa
4000 psi
Overlap, Copper MEK/abrade/MEK
27.6 MPa
4000 psi
Overlap, Brass CDA 260
27.6 MPa
4000 psi
Overlap, Stainless Steel MEK/abrade/MEK
29.0 MPa
4200 psi
Overlap, Brass Cartridge
31.0 MPa
4500 psi
Overlap, Aluminum Etched
31.0 MPa

@Temperature 23.0 °C
 4500 psi

@Temperature 73.4 °F
 Aluminum, Overlap
31.0 MPa

@Temperature -55.0 °C
 4500 psi

@Temperature -67.0 °F
 Aluminum, Overlap
1.52 MPa

@Temperature 121 °C,
Time 900 sec
 220 psi

@Temperature 250 °F,
Time 0.250 hour
 Aluminum, Overlap
4.83 MPa

@Temperature 82.0 °C,
Time 900 sec
 700 psi

@Temperature 180 °F,
Time 0.250 hour
 Aluminum, Overlap
6.89 MPa

@Time 1800 sec
 1000 psi

@Time 0.500 hour
 Aluminum, Overlap
9.65 MPa

@Time 3600 sec
 1400 psi

@Time 1.00 hour
 Aluminum, Overlap
17.2 MPa

@Time 14400 sec
 2500 psi

@Time 4.00 hour
 Aluminum, Overlap
Peel Strength 4.38 kN/m
25.0 pli
7.01 kN/m
40.0 pli
T-Peel, CRS MEK/abrade/MEK, 5-8 mil bondline
8.77 kN/m
50.0 pli
T-Peel, CRS Oakite degreased, 5-8 mil bondline
10.5 kN/m
60.0 pli
T-Peel, Etched Aluminum, 17-20 mil bondline
0.526 - 0.877 kN/m

@Temperature 82.0 °C
 3.00 - 5.00 pli

@Temperature 180 °F
 Aluminum, T-Peel
0.877 - 1.75 kN/m

@Temperature -55.0 °C
 5.00 - 10.0 pli

@Temperature -67.0 °F
 Aluminum, T-Peel
10.5 kN/m

@Temperature 23.0 °C
 60.0 pli

@Temperature 73.4 °F
 Aluminum, T-Peel
Thermal Properties Metric English Comments
CTE, linear 59.0 µm/m-°C
32.8 µin/in-°F
Below Tg
159 µm/m-°C
88.3 µin/in-°F
Above Tg
Thermal Conductivity 0.180 W/m-K

@Temperature 45.0 °C
 1.25 BTU-in/hr-ft²-°F

@Temperature 113 °F
Electrical Properties Metric English Comments
Volume Resistivity 2.40e+14 ohm-cm
2.40e+14 ohm-cm
ASTM D257
Dielectric Strength 43.3 kV/mm
1100 kV/in
ASTM D149
Descriptive Properties Value Comments
Appearance Amber
Accelerator
Opaque, off-white
White
Base