3M Scotch-Weld™ DP125 Translucent Epoxy Adhesive

Category	Polymer , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer	3M
Trade Name	Scotch-Weld™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Scotch-Weld™ DP125 Translucent Epoxy Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

3M™ Scotch-Weld™ Epoxy Adhesive DP125 Translucent is a faster curing version of 3M Scotch-Weld Epoxy Adhesive 2216 Translucent B/A. The worklife and cure time has been reduced from hours and days for the Scotch-Weld epoxy adhesive 2216 Translucent B/A to minutes and hours. Final shear and peel strengths remain similar or even slightly improved compared to the Scotch-Weld epoxy adhesive 2216 Translucent.Information provided by 3M

Physical Properties	Metric	English	Comments
Brookfield Viscosity	2000 - 8000 cP	2000 - 8000 cP	Base, RVF #7 spindle, 20 rpm @ 27°C
	22000 - 33000 cP	22000 - 33000 cP	Accelerator, RVF #7 spindle, 20 rpm @ 27°C

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	55	55	ASTM D2240
Tensile Strength at Break	17.2 MPa	2490 psi	ASTM D882
Elongation at Break	150 %	150 %	ASTM D882
Shear Strength	0.172 MPa	25.0 psi	Overlap, Polypropylene
	1.38 MPa	200 psi	Overlap, +3M Primer 3901
	1.72 MPa	250 psi	Overlap, Glass, Borosilicate
	2.90 MPa	420 psi	Overlap, Acrylic
	3.17 MPa	460 psi	Overlap, ABS
	3.45 MPa	500 psi	Overlap, PVC
	4.83 MPa	700 psi	Overlap, Wood, Fir
	4.83 MPa	700 psi	Overlap, Polycarbonate
	8.27 MPa	1200 psi	Overlap, Fiberglass
	9.65 MPa	1400 psi	Overlap, Sanded Aluminum
	10.3 MPa	1500 psi	Overlap, Cold Rolled Steel
	17.2 MPa	2500 psi	Overlap, Etched Aluminum
	1.03 MPa @Temperature 82.0 °C	150 psi @Temperature 180 °F	Overlap
	1.31 MPa @Temperature 66.0 °C	190 psi @Temperature 151 °F	Overlap
	2.76 MPa @Temperature 49.0 °C	400 psi @Temperature 120 °F	Overlap
	17.2 MPa @Temperature 21.0 °C	2500 psi @Temperature 69.8 °F	Overlap
	27.6 MPa @Temperature -55.0 °C	4000 psi @Temperature -67.0 °F	Overlap
Peel Strength	0.351 kN/m	2.00 pli	180°
	0.526 kN/m	3.00 pli	180°
	0.526 kN/m	3.00 pli	180°
	1.75 kN/m	10.0 pli	180°
	6.14 kN/m	35.0 pli	180°

Thermal Properties	Metric	English	Comments
CTE, linear	112 µm/m-°C @Temperature 5.00 - 20.0 °C	62.2 µin/in-°F @Temperature 41.0 - 68.0 °F	Below Tg
	190 µm/m-°C @Temperature 65.0 - 140 °C	106 µin/in-°F @Temperature 149 - 284 °F	Above Tg
Thermal Conductivity	0.154 W/m-K @Thickness 6.35 mm, Temperature 44.3 °C	1.07 BTU-in/hr-ft²-°F @Thickness 0.250 in, Temperature 112 °F
Glass Transition Temp, Tg	3.00 °C	37.4 °F	Onset
	15.0 °C	59.0 °F	Mid-Point

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.20e+11 ohm-cm	1.20e+11 ohm-cm	ASTM D257
Dielectric Constant	6.3 @Frequency 1000 Hz	6.3 @Frequency 1000 Hz	ASTM D150
Dielectric Strength	30.1 kV/mm @Thickness 0.762 mm	765 kV/in @Thickness 0.0300 in	ASTM D149

Processing Properties	Metric	English	Comments
Cure Time	120 min	2.00 hour	Tack-free
	150 min	2.50 hour	Time to Handling Strength
	420 min	7.00 hour	Full

Descriptive Properties	Value	Comments
Appearance	Amber	Accelerator
	Clear	Base
	Translucent