Cosmic Plastics 6230F Long Glass Fiber Filled Iso Diallyl Phthalate Molding Compound

Category Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Long Glass Fiber Filled , Filled/Reinforced Thermoset
Manufacturer Cosmic Plastics
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Cosmic Plastics 6230F Long Glass Fiber Filled Iso Diallyl Phthalate Molding Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer.
Physical Properties Metric English Comments
Density 1.82 g/cc
0.0658 lb/in³
Apparent Bulk Density 0.300 g/cc
0.0108 lb/in³
Water Absorption 0.27 %
0.27 %
48 hrs, 50°C
Linear Mold Shrinkage 0.0010 - 0.0040 cm/cm
0.0010 - 0.0040 in/in
typical.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 41.0 - 55.0 MPa
5950 - 7980 psi
Flexural Strength 103 MPa
14900 psi
Compressive Strength 186 MPa
27000 psi
Izod Impact, Notched 2.40 J/cm
4.50 ft-lb/in
Thermal Properties Metric English Comments
CTE, linear 24.0 µm/m-°C

@Temperature 20.0 °C
13.3 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 1.8 MPa (264 psi) 260 °C
500 °F
Heat Distortion temperature
Flammability, UL94 V-0

@Thickness 3.20 mm
V-0

@Thickness 0.126 in
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+17 ohm-cm
>= 1.00e+17 ohm-cm
Surface Resistance >= 1.00e+17 ohm
>= 1.00e+17 ohm
Dielectric Constant 4.0

@Frequency 1e+6 Hz
4.0

@Frequency 1e+6 Hz
Wet
4.2

@Frequency 1000 Hz
4.2

@Frequency 1000 Hz
Wet
Dielectric Strength 16.0 kV/mm
406 kV/in
Wet, Step by Step
Dissipation Factor 0.010

@Frequency 1000 Hz
0.010

@Frequency 1000 Hz
Wet
0.013

@Frequency 1e+6 Hz
0.013

@Frequency 1e+6 Hz
Wet
Arc Resistance 180 sec
180 sec
Processing Properties Metric English Comments
Processing Temperature 135 - 165 °C
275 - 329 °F
Molding temperature